Orientador: Renato Mazzonetto / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T06:05:49Z (GMT). No. of bitstreams: 1
Kluppel_LeandroEduardo_M.pdf: 14531516 bytes, checksum: c01e828bcc790ef759e104126e1ff65a (MD5)
Previous issue date: 2007 / Resumo: O objetivo deste estudo foi analisar histológica e radiograficamente a influência do tamanho das partículas da matriz óssea bovina anorgânica (MOBA) sobre o processo de reparação óssea. Na calvária de 18 coelhos adultos da raça Nova Zelândia foram preparadas quatro cavidades com diâmetro de 8 milímetros, sendo duas do lado direito da sutura sagital e duas do lado esquerdo. Os defeitos foram preenchidos com osso autógeno triturado (grupo controle); MOBA de granulação grossa; MOBA de granulação média ou MOBA de granulação fina. Os animais foram sacrificados nos períodos pós-operatórios de 15, 30 e 60 dias. Antes do início do processamento histológico, as peças foram radiografadas sequencialmente. Para análise destas imagens utilizou-se como padrão de comparação o osso do crânio que não estava envolvido nas áreas de ostectomia. Desta forma, observou-se que o osso autógeno apresentava-se discretamente radiopaco inicialmente, tendendo a apresentar uma radiopacidade bastante semelhante ao tecido adjacente no período final. A MOBA de granulação grossa e média mantiveram o mesmo padrão radiográfico, sendo que aos 60 dias, o aparecimento de uma porção radiolúcida em sua porção central pode ser observada. Já a MOBA de granulação fina apresentava discreta radiolucidez no período inicial, a qual tornou-se mais intensa nos períodos sucessivos. A análise histológica demonstrou a formação de maior quantidade de osso e menos reação inflamatória no grupo controle (osso autógeno). Para o biomaterial, em todas as granulações pôde-se observar a presença de infiltrado inflamatório considerável nos períodos de 15 e 30 dias. Nos defeitos preenchidos pela MOBA de granulações grossa e média o processo de reparação transcorreu de maneira semelhante, sendo que no período final uma grande quantidade de partículas e tecido conjuntivo fibroso ainda estavam presentes na cavidade. Contrariamente, a MOBA de granulação fina proporcionou a formação de maior quantidade de tecido osteóide e as partículas foram reabsorvidas quase que em sua totalidade transcorridos 60 dias de sua implantação. Com base nos resultados obtidos, conclui-se que: (1) o enxerto ósseo autógeno isoladamente proporcionou o melhor resultado em termos de reparação dos defeitos ósseos; (2) a MOBA é um material biocompatível; (3) a MOBA de granulação grossa e média não são reabsorvidas em sua totalidade no período observado; (4) a MOBA de granulação fina foi reabsorvida de forma mais intensa e proporcionou uma maior formação de tecido osteóide quando comparada às outras granulações / Abstract: The aim of this present study was to analyze, clinical and histologically, the influence of anorganic bovine bone matrix (ABBM) particle size on bone repair. Four calvarial defects of 8 millimeters each were prepared in 18 adult New Zealand rabbits, two in the right side, and two in the left side. The defects were filled with either particulate autogenous bone (control group); ABBM of large size granules; ABBM of medium size granules; or ABBM of small size granules. The animals were sacrificed at 15, 30, and 60 days after surgery. The samples were radiographic examined before being submitted to histological processing. The analysis of these radiographic images was performed by comparing them with images of the cranial bone not involved with the areas of osteotomy. Thus, it was observed that autogenous bone showed a slight radiopacity at the beginning which was increased at the final period, being very similar to the adjacent bone tissue in terms of radiopacity. The large and medium size ABBM particles maintained the same radiographic behavior, showing a radiolucid area in the central portion of the defect at 60 days. On the other hand, the ABBM of small size granules showed a slight radiolucity at the initial period, which was increased at the subsequent periods. The histological analysis showed a more intense bone formation within the control group (autogenous bone). With regards to the biomaterial, it was observed that all three particle sizes resulted in inflammatory infiltration at 15 and 30 days. The bone repair at the defects filled with ABBM of medium or large size granules was similar to each other, with the presence of a large amount of remaining particles and fibrous connective tissue in the defect at the final period. In contrast, ABBM of small size granules lead to a greater amount of osteoid tissue, and the particles were almost totally reabsorbed within 60 days of implantation. Based on these results, it was concluded that: (1) autogenous bone graft lead to the best result in terms of bone defect repair; (2) ABBM is a biocompatible material; (3) ABBM of large and medium size granules are not totally reabsorbed at the observed period; (4) ABBM of small size granules was more intensively reabsorbed, and lead to a greater osteoid tissue formation when compared to the medium and large ABBM granules / Mestrado / Cirurgia e Traumatologia Buco-Maxilo-Faciais / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288695 |
| Date | 02 September 2007 |
| Creators | Kluppel, Leandro Eduardo |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Mazzonetto, Renato, 1968-2011, Gabrielli, Marisa Aparecida Cabrini, Albergaria-Barbosa, José Ricardo de |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 57f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds