Previous issue date: 2017-08-28 / Capes / A interação dos materiais utilizados na fabricação de equipamentos com os ambientes para os quais são colocados em serviço frequentemente causa sua degradação. A fragilização por hidrogênio apresenta-se como um processo de degradação caracterizado pela nucleação e propagação de trincas nos materiais metálicos, como em tubulações utilizadas no setor de petróleo e gás, sendo classificada como uma das mais perigosas para a integridade estrutural, uma vez que pode ocorrer de forma repentina de difícil percepção, resultando em fratura catastrófica. Por conseguinte, é necessário envidar esforços para obter parâmetros e critérios que ajudam na seleção, inspeção e manutenção de equipamentos, onde as condições operacionais favoreçam a ocorrência de um ambiente de fratura assistida. Para isso, foram realizados ensaios com o aço API 5CT P110, pré-dopado com hidrogênio, seguido pela metodologia de passo incremental (step loading), norma ASTM F1624 (2012), em água do mar sintética com superproteção catódica. A solução de água do mar foi preparada de acordo com a norma ASTM D1141 (2013). O início de crescimento de trinca subcrítico foi determinado através da técnica de queda de potencial de corrente alternada. Os resultados mostraram uma diminuição importante na tenacidade à fratura de iniciação do aço e validaram a determinação do limiar de intensidade de tensões (KIHAC) do aço API 5CT P110 em água do mar sintética sob superproteção catódica. / The interaction of materials used in the fabrication of equipment with the environments for which they are put into service often causes their degradation. The hydrogen embrittlement presents as a degradation process characterized by the nucleation and propagation of cracks in metallic materials, as in pipes used in the oil and gas sector, being classified as one of the most dangerous for structural integrity, since it can occurring suddenly and difficult to perceive, resulting in a catastrophic fracture. Therefore, it is necessary to make efforts to obtain parameters and criteria that help in the selection, inspection and maintenance of equipment, where the operating conditions favor the occurrence of an assisted fracture environment. For this, tests were carried out with the API 5CT P110 steel, pre-doped with hydrogen, followed by step loading methodology, ASTM standard F1624 (2012), in synthetic sea water with cathodic overprotection. The seawater solution was prepared in accordance with ASTM D1141 (2013). The beginning of subcritical crack growth was determined by the technique of alternating current potential drop. The results showed a significant decrease in the steel initiation fracture toughness and validated the determination of the stress intensity threshold (KIHAC) of the API 5CT P110 steel in synthetic sea water under cathodic overprotection.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/363 |
| Date | 11 April 2018 |
| Creators | OLIVEIRA, Misael Souto de. |
| Contributors | SILVA, Antonio Almeida., SANTOS, Marco Antonio dos., MELO, João Baptista Agra de., CARRASCO, Jorge Antonio Palma. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.024 seconds