Orientador: Mário Alexandre Coelho Sinhoreti / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-18T20:32:55Z (GMT). No. of bitstreams: 1
Bosquiroli_Virginia_D.pdf: 701751 bytes, checksum: 2307f95279a8edcdf7bb8467a7c89fd7 (MD5)
Previous issue date: 2011 / Resumo: O objetivo neste estudo foi analisar as propriedades mecânicas (microdureza, resistência coesiva, rugosidade e perda de massa por abrasão) e a resistência da união entre dente/restauração de diferentes resinas compostas. Para os testes de resistência da união e micro-dureza, trinta incisivos bovinos foram usados para três grupos experimentais (n=10). Cavidades tronco-cônicas (2,0 mm de altura x 2,0 mm de diâmetro maior x 1,5 mm de diâmetro menor) foram preparadas e restauradas com os seguintes sistemas adesivos e resinas compostas (Single Bond 2 e Z100; Single Bond 2 e Filtek Z350 e; P90 System Adhesive e Filtek P90 - 3M/ESPE), de acordo com as recomendações do fabricante. A fonte de luz LED Freelight 2 (3M/ESPE) foi usada para a fotoativação dos compósitos, durante 40 s. Após serem armazenados em estufa emergidos em água destilada a 37oC durante 24 h os corpos de prova receberam polimento e mensurações de microdureza (KHN) foram feitas no topo e na base ( HMV-2, Shimadzu, Tokyo). Em seguida, foram realizados nestes corpos de prova o teste de resistência de união push-out em uma máquina de ensaio universal (Instron modelo 4411, MA, USA). Os valores de resistência de união foram submetidos à análise de variância ANOVA 1-critério e os de KHN a análise de variância ANOVA 2-critérios, seguidos do teste de Tukey a 5%. A Filtek P90 mostrou o maior valor de resistência de união e menor em dureza Knoop diferindo estatisticamente das demais resinas compostas. A Filtek Z350 obteve valor de resistência de união e dureza Knoop intermediário entre as resinas compostas avaliadas. A Z100 obteve o menor valor de resistência de união e o maior valor de dureza Knoop diferindo estatisticamente das demais resinas compostas e diferindo entre valor de topo e base no próprio compósito. Para confeccionar as amostras para o teste de resistência coesiva (RC) foi preparado um molde de silicone com formato de ampulheta com 11 mm de comprimento, 2 mm de largura, 1 mm de espessura e 1 mm na região de constrição. Para mensuração de rugosidade de superfície (Ra) e perda de massa (PM), antes e após a escovação, foi preparado moldes de silicone com 5 mm de diâmetro e 2 mm de espessura. Todas as amostras foram polidas com lixas de SiC 2000 e estocadas em estufa emergidas em água destilada a 37 oC por 24 h. Para Ra e PM, após o ciclo de escovação, os corpos de prova foram armazenados em estufa emergidos em água destilada a 37 oC por 24 antes da mensuração final sendo limpos em ultrassom por 15 min e removida a umidade superficial com papel absorvente. A RC foi realizada em máquina de ensaio universal (Instron modelo 4411, MA, USA). Os dados obtidos de cada teste foram submetidas a análise de variância ANOVA 1- critério e teste de Tukey a 5%. A Filtek Z350 e Z100 obtiveram os maiores valores de RC superiores a Filtek P90 e não diferindo estatisticamente entre sí. A Filtek Z350 teve o menor aumento de Ra e a Filtek P90 obteve os maiores valores de PM diferindo estatisticamente das demais resinas compostas. Pode-se concluir que tanto a matriz orgânica como a partícula de carga podem influenciar nas propriedades mecânicas e na resistência de união de restaurações de resina composta / Abstract: The aim of this study was to analyze the mechanical properties (micro-hardness, cohesive strength, surface roughness and loss mass through abrasion) and the bond strength between tooth/restoration of different composite resins. For bond strength and micro-hardness analyzes, thirty bovine incisors were used for three experimental groups (n=10). Trunk- conical cavities (2,0 x 2,0 x 1,5 mm) were prepared and restored with the following adhesive systems and resin compounds (Single Bond 2 and Z100; Single Bond 2 and Filtek Z350 and; P90 System Adhesive and Filtek P90 - 3M/ESPE), following manufacture's recommendations. A LED Freelight 2 (3M/ESPE) was used for the photo-activation of the composites for 40 s. After being emerged in distilled water and stored in an incubator at 37o C for 24 hours, the specimens were polished and micro-hardness measurements (KHN) were taken at the top and base ( HMV-2, Shimadzu, Tokyo). After that, the push-out resistance test was performed with a universal testing machine (Instron modelo 4411, MA, USA). Bond strength values were submitted to a variance analysis ANOVA 1-way, and KHN to the variance analysis ANOVA 2-way followed by the Tukey's test at 5% level of significance. Filtek P90 showed the highest bond strength value and the lowest Knoop hardness values differing statistically from the others composite resins. Filtek Z350 obtained bond strength values and KHN values intermediate among the other resin composites. Z100 showed the lowest bond strength values and highest Knoop hardness value statically different from the others composite resins and differing from top and bottom values in itself. To prepare the specimens for the cohesive strength test (CS), an hourglass silicone mold was made measuring 11 mm in length by 2 mm wide, and 1 mm thick by 1mm wide in the narrowed region. To measure surface rugosity (Ra) and mass loss (ML) before and after brushing, silicone molds were prepared measuring 5 mm in diameter by 2 mm thick. All samples were polished with SiC 2000 sandpaper and emerged in distilled water and stored in an incubator at 37o C for 24 hours. For Ra and ML, after the brushing cycle, the specimens were emerged in distilled water and stored in an incubator at 37o C for 24 hours before the final measurements being cleaned in ultrasonic immersion for 15 minutes and having the surface moisture removed with absorbent paper. CS was performed in a universal testing machine (Instron modelo 4411, MA, USA). The obtained data were submitted to the ANOVA 1-way analysis and the Turkey test at 5% level significance. Filtek Z350 and Z100 obtained higher CS values than Filtek P90 without statistically difference among each other. Filtek Z350 showed the lowest increase of Ra and Filtek P90 the highest ML values differing statistically from the others composite resins. It can be concluded that both the organic matrix and the type of particle filler can influence in the mechanical properties and bond strength of resin composite restorations / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288135 |
| Date | 18 August 2018 |
| Creators | Bosquiroli, Virginia, 1970- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Sinhoreti, Mário Alexandre Coelho, 1969-, Konno, Alysson Noriyuky Kajishima, Brandt, William Cunha, Consani, Rafael Leonardo Xediek, Pascon, Fernanda Miori |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 38 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0032 seconds