Magnetic nanoparticles (MNPs) hold great promise in the fields of biology and medicine. The synthesis of functional MNPs with precisely controlled crystallographic, physicochemical, and magnetic properties on a large scale still remains the challenge today. This thesis reports the exploration of liquid-fed flame spray pyrolysis (FSP) in the synthesis of functional MNPs, their surface modifications, and potential bio-applications. Superparamagnetic and ferromagnetic maghemite (γ-Fe2O3) nanoparticles, and silica-coated maghemite (SiO2/γ-Fe2O3) nanocomposites were synthesised using FSP. The size of γ-Fe2O3 was controllable from 6 to 53 nm, with morphology evolving from a disordered near-spherical shape to fully ordered 2-D hexagonal/octagonal platelet. The saturation magnetisation (Ms) increased from 21 to 74 emu/g with increasing particle size, up to 13 nm when Ms approached the bulk γ-Fe2O3 characteristics. In the case of SiO2/γ-Fe2O3, three distinct morphologies, namely the single segregated γ-Fe2O3 core- SiO2 shell, transitional mixed morphologies, and multi γ-Fe2O3 cores embedded in submicron SiO2 shell, were obtained. The core size, composite size, and morphology of γ- Fe2O3 were tunable by varying %SiO2 loading and the use of a quartz tube enclosure during flame synthesis. The magnetic behaviour correlated well with the crystal microstructure. Following the core particle design, protein adsorption-desorption behaviour on FSP-madeMNPs was studied. Bovine serum albumin (BSA) adsorption was found to follow the Langmuir isotherm, with high binding capacities (150−348 mg BSA/g particle) and fast association constants. Electrostatically governed BSA orientations were proposed for different particle-buffer systems. The adsorbed BSA was effectively recovered by pH-shift using K2HPO4. Subsequently, terminal amine, aldehyde, carboxylic, epoxy, mercapto and maleimide functionality were anchored onto the FSP-made γ-Fe2O3 particles. These versatile functional groups led to conjugation of active trypsin. The immobilised trypsin exhibited superior durability with >60% residual activity after one week, and excellent reusability for >5 cycles. The trypsin-conjugated MNPs are promising carriers in proteomics, demonstrating good substrate specificity with equivalent or better sequence coverage compared to free trypsin in insulin and BSA digestion. In another application, a refined silanisation procedure simultaneously reduced γ-Fe2O3 to Fe3O4, and generated thiol enriched surface for matrix metalloproteinase-2 (MMP-2) conjugation. The highly active MMP-2-conjugated MNPs could potentially enhance the interstitial transport of macromolecule/nanoparticles in drug delivery.
| Identifer | oai:union.ndltd.org:ADTP/258239 |
| Date | January 2009 |
| Creators | Li, Dan, Chemical Sciences & Engineering, Faculty of Engineering, UNSW |
| Publisher | Publisher:University of New South Wales. Chemical Sciences & Engineering |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | http://unsworks.unsw.edu.au/copyright, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0016 seconds