On the surface quality of continuously cast steels and phosphor bronzes

This thesis work concerns about the importance of the cast surfaces, surface phenomenon such as the formation of the oscillation marks and exudation and related defects including cracks and segregation that happened during the continuous casting. All of the investigated materials were collected during the plant trials while an in-depth analysis on these materials was performed at the laboratory scale with certain explanations supported by the schematic and theoretical models. The work consists on different material classes such as steels and phosphor bronzes with a focus on the surface defects and their improvements. In order to facilitate the theoretical analysis which could be capable of explaining the suggested phenomenon in the thesis, a reduced model is developed which required lesser computational resources with lesser convergence problems. / <p>QC 20160527</p> / Oscilation mark formation during continous casting of steel

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-187718
Date January 2016
CreatorsSaleem, Saud
PublisherKTH, Metallernas gjutning, Stockholm
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeDoctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0019 seconds