An apparatus utilizing a constant pressure flow system was developed for measuring the effect of pressure on the diffusion rates, and therefore diffusion coefficients, of binary gas mixtures passing through porous solids.
Hydrogen and nitrogen were employed for testing ceramic porous solids at room temperature, with various pressures from 1 to 14.6 atmospheres absolute. The values obtained for the products of the effective diffusion coefficients and absolute pressures were substantially constant, with a maximum deviation of ±5%. It seemed that the diffusion rate of hydrogen increased with pressure, while that of nitrogen decreased. At atmospheric pressure the ratio of diffusion rates {N(H₂)/N(N₂)} was in good agreement with the theoretical value proposed by Hoogschagen i.e. √M(N₂)/M(H₂).
However, the experimental diffusion ratio increased with pressure. This behavior might be due to some degree of forced flow present in the diffusion process, although it was not possible to determine a cause for such a flow.
This apparatus is suitable for the study of diffusion rates in the transition region, between Knudsen and ordinary diffusion, by simply changing pressure and hence the mean free path of the gases involved. Forced flow would not be a factor in this region. / Applied Science, Faculty of / Chemical and Biological Engineering, Department of / Graduate
Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/41047 |
Date | January 1959 |
Creators | Han, Agnes Yu-Wen |
Publisher | University of British Columbia |
Source Sets | University of British Columbia |
Language | English |
Detected Language | English |
Type | Text, Thesis/Dissertation |
Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0019 seconds