Nano-scale temperature dependent visco-elastic properties of polyethylene terephthalate (PET) using atomic force microscope (AFM).

Visco-elastic behaviour at the nano-level of a commonly used polymer (PET) is characterised using atomic force microscopy (AFM) at a range of temperatures. The modulus, indentation creep and relaxation time of the PET film (thickness = 100 m) is highly sensitive to temperature over an experimental temperature range of 22¿175 ¿C. The analysis showed a 40-fold increase in the amount of indentation creep on raising the temperature from 22 ¿C to 100 ¿C, with the most rapid rise occurring above the glass-to-rubber transition temperature (Tg = 77.1 ¿C). At higher temperatures, close to the crystallisation temperature (Tc = 134.7 ¿C), the indentation creep reduced to levels similar to those at temperatures below Tg. The calculated relaxation time showed a similar temperature dependence, rising from 0.6 s below Tg to 1.2 s between Tg and Tc and falling back to 0.6 s above Tc. Whereas, the recorded modulus of the thick polymer film decreases above Tg, subsequently increasing near Tc. These visco-elastic parameters are obtained via mechanical modelling of the creep curves and are correlated to the thermal phase changes that occur in PET, as revealed by differential scanning calorimetry (DSC).

Identiferoai:union.ndltd.org:BRADFORD/oai:bradscholars.brad.ac.uk:10454/5493
Date2012 June 1920
CreatorsGrant, Colin, A., Alfouzan, Abdulrahman, Twigg, Peter C., Coates, Philip D., Gough, Timothy D.
Source SetsBradford Scholars
LanguageEnglish
Detected LanguageEnglish
TypeArticle, published version paper
Relationhttp://www.sciencedirect.com/science/article/pii/S0968432812001783

Page generated in 0.002 seconds