An adsorbent for Cs removal from contaminated water based on phosphotungstic acid (PTA) embedded in SiO 2 network was synthesized and granulated with γ-Al 2 O 3 . PTA/SiO 2 had a high adsorption capacity towards Cs while the binder provided excellent mechanical characteristics of the material. It was shown that small particles of PTA/SiO 2 with the sizes of 0.1–1 µm occupied space between larger particles of the binder (up to 5 µm). Chemical interaction between PTA and γ-Al 2 O 3 during the adsorbent preparation also took place. The obtained porous material with the specific surface area of 286.9 m 2 /g contained 4.73% of PTA. Presence of Keggin units in the structure was confirmed by solid state NMR spectroscopy. Study of the adsorbent in Cs + adsorption from solutions demonstrated its high adsorption capacity. The concentrations of Cs + in the solutions after the column tests decreased by 3.3–5.2 times. The presence of Na + and K + as competing ions did not affect the adsorption. The material was tested in clean-up of radioactive water from the shelter of Chernobyl nuclear power plant (Ukraine). A significant decrease of 137 Cs radioactivity was detected in all samples of radioactive water, especially in acidic solutions. Thus the adsorbent can be used for water treatment after incidents resulting in release of radioactive isotopes 134 Cs and 137 Cs.
| Identifer | oai:union.ndltd.org:ETSU/oai:dc.etsu.edu:etsu-works-11258 |
| Date | 01 April 2019 |
| Creators | Little, Iuliia, Alorkpa, Esther, Khan, Valerii, Povazhnyi, Volodymyr, Vasiliev, Aleksey |
| Publisher | Digital Commons @ East Tennessee State University |
| Source Sets | East Tennessee State University |
| Detected Language | English |
| Type | text |
| Source | ETSU Faculty Works |
Page generated in 0.0023 seconds