Garcia, Gilson Piqueras. Efeito do tratamento de polímeros em plasmas de nitrogênio 2018. Tese (Doutorado).pdf: 3148171 bytes, checksum: 4ca44c01e1ec375c08f9b89261de68f3 (MD5) / Approved for entry into archive by Lucimara Kurokawa Shinoda null (lucimaraks@sorocaba.unesp.br) on 2018-03-14T17:38:12Z (GMT) No. of bitstreams: 1
garcia_gp_dr_soro.pdf: 3148171 bytes, checksum: 4ca44c01e1ec375c08f9b89261de68f3 (MD5) / Made available in DSpace on 2018-03-14T17:38:12Z (GMT). No. of bitstreams: 1
garcia_gp_dr_soro.pdf: 3148171 bytes, checksum: 4ca44c01e1ec375c08f9b89261de68f3 (MD5)
Previous issue date: 2018-02-20 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O politetrafluoretileno (PTFE) e a poliamida 6 (PA 6) são polímeros que têm excelentes qualidades mecânicas, elétricas e químicas. Por isto, são utilizados em diversos componentes de equipamentos mecânicos e elétricos entre várias outras aplicações. Entretanto o PTFE possui um ângulo de contato com a água (WCA) de cerca de 120º e a PA 6 um WCA de cerca de 60º. Isto, especialmente no caso do PTFE, diminui a sua adesividade com outros materiais. Para resolver este problema várias técnicas têm sido sugeridas, como, por exemplo, tratamentos químicos e tratamento a plasma. Entre elas o tratamento a plasma, que tem a vantagem de produzir modificações apenas na superfície, não alterando o interior do material. O objetivo deste trabalho é estudar como o WCA varia em função dos parâmetros do tratamento a plasma de nitrogênio, a pressão do gás (p), a potência (P) e o tempo de tratamento (t). O nitrogênio foi escolhido por ser um gás cujo plasma, segundo a literatura, causa reduções significativas no ângulo de contato da superfície de polímeros. Várias séries de tratamento foram conduzidas, tanto para o PTFE quanto para a PA 6. Foram obtidas reduções significativas no WCA, ocorrendo o resultado notável de WCA = 0º para p = 2,6 Pa, P = 300 W e t = 30 min, tanto para o PTFE quanto para a PA 6. Em função dos resultados, dentro do intervalo de parâmetros utilizado, concluiu-se que, de uma forma geral, o WCA diminui com a potência e com o tempo de tratamento, e que o WCA tem um comportamento notável em função da pressão do gás, diminuindo inicialmente até atingir o valor mínimo (ótimo) de 0º para p = 2,6 Pa, e então passa a crescer a partir deste ponto. A redução do WCA das amostras tratadas foi consequência do aumento da energia de superfície, motivado pela incorporação de funções nitrogenadas e oxigenadas nas suas superfícies. A Espectroscopia de fotoelétrons excitados por raios X (XPS) foi usada para caracterizar a composição e estrutura da superfície do PTFE e da PA 6. A rugosidade e o ângulo de contato dos polímeros foram medidos por perfilometria e goniometria, respectivamente. A análise XPS mostrou, para o PTFE, que houve incorporação de oxigênio e nitrogênio, para a PA 6, o aumento da concentração de oxigênio, e para ambos, a presença de grupos químicos polares em sua superfície. As medições do WCA em função do tempo decorrido após o de tratamento, mostraram que, para o PTFE e para a PA 6, o WCA volta a crescer, estabilizando em torno de 90 dias, quando, para o PTFE atinge cerca de 80% do WCA da amostra sem tratamento. A PA 6 apresentou um resultado notável, com o WCA estabilizando com um valor de cerca do dobro do valor do WCA da amostra sem tratamento, o que transforma a sua superfície de hidrofílica para hidrofóbica, possibilitando novas possibilidades de usos em engenharia. / Polytetrafluoroethylene (PTFE) and polyamide 6 (PA 6) are polymers that have excellent mechanical, electrical and chemical properties. Therefore, they are used in diverse mechanical and electrical equipment components among many other applications. However, PTFE has a water contact angle (WCA) about of 120º and PA 6 has a WCA about of 60º. This, especially for PTFE, decreases their adhesiveness with other materials. To solve this problem, many techniques have been proposed, such as chemical and plasma treatments. Among them the plasma treatment has the advantage of producing modifications on the surface only, altering the bulk. The objective of this work is to study how the WCA varies as a function of the nitrogen plasma treatment parameters, the gas pressure (p), the applied power (P) and the treatment time (t). Nitrogen plasmas were used in this study since, according the literature, such plasmas significantly reduce the surface contact angle of polymers. Several series of treatment were conducted, for PTFE as for PA 6. Significant reductions in WCA were obtained, including a WCA of 0º notable for p = 2.6 Pa, P = 300 W and t = 30 min, for PTFE as for PA 6. Thus, from the results, within the range of the parameters studied, it was concluded that, in general, the WCA diminishes as the power and as the treatment time increases, and that the WCA has a notable behavior as a function of the gas pressure, initially decreasing to reach a minimum (optimum) value of 0 º for p = 2.6 Pa, and then increasing after this point. The reduction in WCA of the treated samples was a consequence of the increase in surface energy, motivated by the incorporation of surface functionalities. X-ray photoelectron spectroscopy (XPS) was used to characterize the structure and composition of the PTFE and PA 6 surfaces. Roughness and surface contact angles of the polymers were measured using profilometry and goniometry, respectively. XPS analyses reveal, for PTFE, the incorporation of oxygen and nitrogen, for PA 6 the increase of oxygen concentration, and for both the presence of polar chemical groups on the treated surface. Measurement of the WCA as a function of the time after the treatment, showed that, for PTFE and PA 6, the WCA tends to increase, stabilizing after about 90 days, when, for PTFE, it reaches about of 80% of the value for virgin PTFE. PA 6 showed a notable result, the WCA stabilized at about double the value of the WCA of virgin PA6, indicating a switch from a hydrophilic to a hydrophobic surface, thus enabling new uses as an engineering polymer.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/153025 |
| Date | 20 February 2018 |
| Creators | Garcia, Gilson Piqueras |
| Contributors | Universidade Estadual Paulista (UNESP), Durrant, Steven Frederick [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600, 600 |
Page generated in 0.002 seconds