This master’s thesis deals with plasticization of poly(3-hydroxybutyrate), polylactid acid and their blend. It explores effect of chemical structure of plasticizer on mechanical properties of this polymer blend and on its diffusion from the polymer blend. Syntheses of plasticizers based on oligomeric polyadipates, citrates, lactate and esters of 2 ethylhexanoic acid with poly(ethyleneglycol) were carried out. Molecular weight distribution of synthesized plasticizers was determined using gel permeation chromatography. Poly(3-hydroxybutyrate), polylactid acid and their blend were plasticized with synthesized and commercial plasticizers. From commercial, chosed plasticizers were based on citrates and ester of 2-ethylhexanoic acid with poly(ethyleneglycol). Thermal stability of selected commercial plasticizers in polylactid acid was studied using thermogravimetry. Diffusion of plasticizers from poly(3-hydroxybutyrate), polylactid acid and their blend during exposure to 110 °C was also investigated. Mechanical properties of prepared blends were tested by tensile test. Almost all used plasticizers showed positive softening effect in blend. The highest elongation at break was detected for the blend with commercial acetyltributylcitrate, where elongation at break reached 328 % relative to 21 % for neat non-plasticized blend.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:438891 |
| Date | January 2018 |
| Creators | Stehnová, Ivana |
| Contributors | Alexy, Pavol, Přikryl, Radek |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds