Investigations into the mechanical properties and curing characteristics of dental glass-ionomer cements

Conventional glass ionomer cements (GICs), which continue to gain acceptance as superbly biocompatible dental materials, were first released in the early 1970s as a result of research into combining the advantages of silicate cements and polyalkenate cements. The chemistry of GICs is based upon the aqueous reaction between an ion-leachable fluoride glass and polyacid which yields the final cross-linked insoluble ionomer (ionic polymer). The significant advantages of GICs include direct adhesion to tooth structures, fluoride release, minimal dimensional change on curing, significant ease of use and superb biocompatibility, to the extent that affected proximal tooth structures may be retained, remineralised , and strengthened against further caries. GICs have, however, been unfavourably compared with other restorative materials in their mechanical properties and setting characteristics, in particular their relative weakness, the time limitations for the acid-base reaction to proceed to acceptable maturity, and the susceptibility of the immature cement to water sorption or desiccation.

Identiferoai:union.ndltd.org:ADTP/269898
CreatorsPrentice, Leon Hugh
Source SetsAustraliasian Digital Theses Program
LanguageEnglish
Detected LanguageEnglish
RightsTerms and Conditions: Copyright in works deposited in the University of Melbourne Eprints Repository (UMER) is retained by the copyright owner. The work may not be altered without permission from the copyright owner. Readers may only, download, print, and save electronic copies of whole works for their own personal non-commercial use. Any use that exceeds these limits requires permission from the copyright owner. Attribution is essential when quoting or paraphrasing from these works., Restricted Access: University of Melbourne Staff and Students Only, Login required please enter your University of Melbourne email username and password in the login boxes at the top righthand of this repository page to access this item.

Page generated in 0.0016 seconds