Yes / Binary and ternary blends of a polylactic acid matrix with polycaprolactone (PCL) and polybutylene succinate (PBS) were produced by twin screw extrusion, containing up to 30 wt% loading. Mechanical, thermal and rheological characterisation techniques were used to quantify properties of the different blend formulations and miscibility was investigated using scanning electron microscopy. PCL is known to act as an impact modifier in PLA but to cause a corresponding reduction in strength. Results showed that addition of both PBS and PCL seperatly caused a reduction in melt viscosity, elastic modulus and tensile strength, but an increase in impact strength and strain at break. Analysis of morphology suggested that immiscibility was evident, particularly at higher PCL and PBS loadings. Results indicated that incorporation of a small loading of PBS had a synergistic effect on the PLA-PCL blend properties. Miscibility was improved and enhanced mechanical properties were observed for a ternary blend containing 5 wt% of both PBS and PCL compared to blends containing 10% of each polymer alone. / Financial support of Floreon- Transforming Packaging Ltd through the PhD sponsorship and materials provision.
| Identifer | oai:union.ndltd.org:BRADFORD/oai:bradscholars.brad.ac.uk:10454/16750 |
| Date | 11 December 2018 |
| Creators | Kassos, Nikolaos, Kelly, Adrian L., Gough, Timothy D., Gill, A.A. |
| Source Sets | Bradford Scholars |
| Language | English |
| Detected Language | English |
| Type | Article, Accepted manuscript |
| Rights | This is an author-created, un-copyedited version of an article accepted for publication/published in Materials Research Express. IOP Publishing Ltd is not responsible for any errors or omissions in this version of the manuscript or any version derived from it. The Version of Record is available online at https://doi.org/10.1088/2053-1591/aaf7c1 |
Page generated in 0.0019 seconds