Linear and branched poly(butylene adipate) polyesters with number-average molecular weights ranging from 700 to 10 000 g/mol, and degrees of branching ranging from very low to hyperbranched were solution cast with PVC to study the effects of chemical structure, molecular weight, end-group functionality, and chain architecture on plasticizing efficiency and durability. Miscibility was evaluated by the existence of a single glass transition temperature and a shift of the carbonyl group absorption band. Desirable mechanical properties were achieved in flexible PVC films containing 40 weight-% of polyester plasticizer. Methyl-ester-terminated polyesters with a low degree of branching and an intermediate molecular weight enhanced the plasticizing efficiency, as shown by greater elongation, good miscibility, and reduced surface segregation. A solid-phase extraction method was developed to extract the low molecular weight products that migrated from pure poly(butylene adipate) and PVC/ poly(butylene adipate) films during aging in water. The effects of branching, molecular weight, end-group functionality, and polydispersity on plasticizer permanence were evaluated by quantification of low molecular weight hydrolysis products, weight loss, surface segregation, and the preservation of material properties during aging. A more migration-resistant polymeric plasticizer was obtained by combining a low degree of branching, hydrolysis-protecting end-groups, and higher molecular weight of the polyester. Films plasticized with a slightly branched polyester showed the best durability and preservation of material and mechanical properties during aging. A high degree of branching resulted in partial miscibility with PVC, poor mechanical properties, and low migration resistance. The thermal stability of polyester-plasticized films was higher than that of films containing a low molecular weight plasticizer, and the stabilizing effect increased with increasing plasticizer concentration. / QC 20100805
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-4272 |
| Date | January 2007 |
| Creators | Lindström, Annika |
| Publisher | KTH, Fiber- och polymerteknik, Stockholm : KTH |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Trita-FPT-Report, 1652-2443 ; 2006:45 |
Page generated in 0.0018 seconds