The diploma thesis deals with the heterogeneous technique of preparation of grafted polypropylene g maleic anhydride (PP-g-MAH). The knowledge of the course of the reaction and its impact on the PP grafting process are summarized in the theoretical part. The preparation of the grafted PP was carried out in a fluidized polymerization reactor at 115 °C, speed of mixing 210 rpm, reaction time 60 min and pressure 6 bar. The amount of grafted MAH was monitored by using a MAH concentration 3 and 5 wt% and an initiator concentration 0.25; 0.5; 1; and 1.5 wt%. Modification efficiency was compared by using 3 types of PP with different particle morphology and specific surface area. By creating the theoretical model, the maximum surface concentration of MAH was calculated and compared with experimental data. Characterization of PP materials was performed by Electron Scanning Microscopy (SEM), Differential Scanning Calorimetry (DSC) and particle surface analysis by BET. Quantitative analysis of grafted MAH was determined by FTIR spectroscopy and acid-base titration.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:376886 |
| Date | January 2018 |
| Creators | Brňák, Matúš |
| Contributors | Petruš, Josef, Kučera, František |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0022 seconds