This diploma thesis investigates the suitability of relaxation tests as a part of complex characterization of hydrogel materials using classical rheology methods. With respect to the current research, creep and three interval thixotropy tests were taken into account. For them, general optimization was done aiming to find an ideal parameter settings. The optimization was performed using physically crosslinked agarose (AG) hydrogel and the tuned tests were also applied to two more samples: hyaluronan (HyA) and polyvinyl alcohol (PVAl) gel. These materials were selected due to their mutually different crosslinking principle. The experiments showed, the AG gel proved to have the best ability to recover after deformation of all studied samples. On the other hand, the HyA gel relaxed the worst. Although the final results of both tests were comparable, the regeneration process itself was different. Hence, the complex relaxation characteristics cannot be described using one of the performed tests alone and both the creep and three interval thixotropy tests have great importance in the scope of complex relaxation behaviour. The obtained results may lead to more precise description of deformation and relaxation, which are frequent phenomena occurring during treatment and application of hydrogel materials.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:414166 |
| Date | January 2020 |
| Creators | Kadlec, Martin |
| Contributors | Kráčalík, Milan, Smilek, Jiří |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0023 seconds