Metalloporphyrin aggregation is critical for triplet-triplet annihilation (TTA) to occur. In order to maximize the efficiency of TTA, to use as a mechanism of photon upconversion in dye-sensitized solar cells, it is important to understand the phenomenon of absorber aggregation. The aggregation of ZnTPP in polymer films was investigated by fluorescence anisotropy and total internal reflection fluorescence microscopy (TIRFM). Single molecule spectroscopy (SMS) and spectromicroscopy were the techniques used to study single molecules and multimolecular aggregates of ZnTPP/ZnTPPS in polymer films/adsorbed on glass substrates.<p>
Fluorescence anisotropy measurements consistently showed depolarized emission from films most concentrated with ZnTPP. This observation was likely a result of energy transfer in and among porphyrin aggregates. Fluorescence intensity decays were also obtained and they illustrated a pattern of decreased fluorescence lifetime (i.e. faster decays) as the concentration of porphyrin in the film increased. These results are consistent with the formation of aggregates, and their increased presence in more concentrated films. The formation of these aggregates quenches the fluorophores fluorescence, resulting in the observed shorter fluorescence lifetimes. <p>
TIRFM was performed to study the structure of these polymer films doped with ZnTPP. It was determined that these films consisted of discrete domains and thus lacked homogeneity, and the presence of aggregates was clearly visible. Time-resolved TIRFM measurements were also performed but no interesting results were collected.<p>
SMS and spectromicroscopy were the final techniques employed to study porphyrin aggregation. Preliminary measurements were performed with polymer films doped with ZnTPP, and the single step decay time trajectories collected indicated that single molecules were being studied. Furthermore, emission spectra of these molecules were collected and they were similar to those obtained for a bulk measurement, but the bands were slightly shifted in comparison. These measurements were repeated with ZnTPPS adsorbed to glass substrates. Two different patterns of decay trajectories were measured: (i) single step decays corresponding to single ZnTPPS molecules and (ii) multi step/complex decays representative of multimolecular aggregates. Emission spectra were also collected for the multimolecular aggregates, and they were consistent with those of an ensemble measurement but slightly blue-shifted. Such a shift is common when studying aggregates on such a highly polar surface. Thus, these results demonstrate that ZnTPPS aggregates form even at concentrations as low as 10-8 M, and can be studied using SMS despite their weak fluorescence emission.
| Identifer | oai:union.ndltd.org:USASK/oai:usask.ca:etd-08212010-090815 |
| Date | 17 September 2010 |
| Creators | O'Brien, Jaclyn Ann |
| Contributors | Burgess, Ian, Paige, Matthew, Steer, Ronald P., Bandy, Brian, Ward, Dale |
| Publisher | University of Saskatchewan |
| Source Sets | University of Saskatchewan Library |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://library.usask.ca/theses/available/etd-08212010-090815/ |
| Rights | unrestricted, I hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to University of Saskatchewan or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report. |
Page generated in 0.0022 seconds