Orientador: Fernanda Paula Collares Queiroz, Theo Guenter Kieckbusch / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-08-11T22:22:43Z (GMT). No. of bitstreams: 1
Bertan_LarissaCanhadas_D.pdf: 3212873 bytes, checksum: fe398494b5ab4899a63848bef01c100a (MD5)
Previous issue date: 2008 / Resumo: Pesquisas sobre biofilmes à base de polímeros surgiram devido ao impacto ambiental aliado à necessidade de reduzir os resíduos sólidos. Atualmente, vários estudos estão voltados ao desenvolvimento de tecnologia que controle o crescimento indesejável de microorganismos, através de embalagens ativas. O objetivo deste trabalho foi obter as melhores formulações para o desenvolvimento de biofilmes ativos e avaliar sua aplicação no acondicionamento de pães de forma. Filmes simples e compostos à base de gelatina, glúten e amido (mandioca, mandioca modificado, milho ceroso e milho ceroso modificado) foram desenvolvidos e caracterizados quanto à permeabilidade ao vapor de água (PVA), permeabilidade ao oxigênio (PO2), solubilidade em água (SOL) e propriedades mecânicas (resistência à tração - RT e porcentagem de elongação - ELO), variando a concentração da macromolécula e do plastificante (glicerol). Os filmes contendo 10 g de gelatina com 5% de glicerol (em relação à massa seca da proteína) e o filme com 5 g de glúten, 32,5 mL de etanol/100 mL de solução, pH 5 e 20% de glicerol (em relação à massa seca da proteína) foram selecionados para a elaboração dos filmes compostos. Filmes compostos de glúten/gelatina (GLU/GEL), amido de mandioca/gelatina (AM/GEL), amido de mandioca modificado/gelatina (AMM/GEL), amido de milho ceroso/gelatina (AMC/GEL), amido de milho ceroso modificado/gelatina (AMCM/GEL) em diversas proporções 1:1, 1:4 e 4:1 e amido/gelatina/glúten (AM/GLU/GEL; AMM/GLU/GEL, AMC/GLU/GEL e AMCM/GEL) na proporção 1:1:1, também foram confeccionados e caracterizados. Os filmes compostos apresentaram menor PVA e maior RT que os filmes simples de gelatina. Os filmes compostos AMM/GEL, GLU/GEL e AMM/GLU/GEL, nas proporções 4:1; 4:1 e 1:1:1, respectivamente, foram utilizados no desenvolvimento de filmes ativos. Os filmes compostos foram adicionados de sorbato de potássio (SP) na concentração de 2 e 4% (p/v). A adição de SP provocou aumento na PVA, na SOL e na ELO e redução na RT, em relação aos filmes sem sorbato. A superfície dos filmes compostos mostrou-se lisa e homogênea, com exceção do filme AMM/GLU/GEL com 4% de SP. Para os testes de difusão em halo, foram isolados 5 fungos: (i) Eurotium chevalieri; (ii) Eurotium amstelodami; (iii) Wallemia sebii; (iv) Penicillium raistrickii e (v) Cladosporium sp. Os filmes que apresentaram maior eficiência na redução do crescimento dos fungos e melhores propriedades de barreira e mecânicas foram: (i) AMM/GEL e (ii) GLU/GEL, ambos com 2% de SP. Os filmes ativos selecionados no teste de difusão em halo apresentaram duas tangentes de perda (tan ?), indicando a existência de duas Tg. Os filmes de GLU/GEL, sem e com 2% SP, foram utilizados no acondicionamento de pão de forma, sendo que as fatias de pães justapostas foram intercaladas com os filmes ativos e colocadas em sacos de polietileno de baixa densidade. O uso de filmes entre as fatias provocou aumento da firmeza, diminuição da umidade e da atividade de água. A análise microbiológica não indicou diferença significativa entre a estocagem com filmes ativos e o controle. No 7° dia, os pães continham a quantidade máxima de SP permitida no produto pela legislação brasileira / Abstract: In recent years the research on polymer-based biofilms has seen considerable increase due to concern over environmental impact and the need to reduce solid residue generation. There are several studies concerning the control of microbial activity in prepared food using active packaging. The objective of this work was to develop the best formulation of active biofilms and to evaluate their performance in sliced bread packaging. Simple and composite films were developed, based on gelatin, gluten and diferent types of starch (cassava, modified cassava, waxy maize and modified waxy maize starches). Films were characterized for their permeability to water vapor (WVP), permeability to oxygen (PO2), solubility in water (SOL) and mechanical properties (tensile strengh -TS and elongation -ELO), using different concentrations of the macromolecules and plasticizer (glycerol). Films containing 10g of gelatin and 5% of glycerol (based on protein dry mass) and films with 5g of gluten, 32.5 mL of ethanol/mL of solution, at pH of 5 and 20% glycerol (based on protein dry mass) were selected for the manufacture of composite films. Composite films of gluten/gelatin (GLU/GEL), cassava starch/gelatin (CS/GEL), modified cassava starch/gelatin (MCS/GEL), waxy maize starch/gelatin (WMS/GEL), modified waxy maize starch/gelatin (MWMS/GEL), at 1:1, 1:4 and 4:1 ratios and starch/gelatin/gluten (S/GLU/GEL) at 1:1:1 ratio were manufactured and characterized. Composite films presented lower WVP and larger RT than simple gelatin film. Composite films based on MCS/GEL, GLU/GEL and MCS/GLU/GEL at 4:1, 4:1 and 1:1:1 ratios, respectively, were used for the development of active films usine, potassium sorbate (PS) at 2 and 4%, in volume concentrations. Addition of PS promoted increase in WVP, SOL and ELO as well as a decrease in TS, when compared to films with no added anti-microbial agent. Surface of the composite films were smooth and homogeneous except for the MCS/GLU/GEL with 4% PS. Five microorganisms were selected, for the diffusion halo assay: (i) Eurotium chevalieri; (ii) Eurotium amstelodami; (iii) Wallemia sebii; (iv) Penicillium raIstrickiI e (v) Cladosporium sp. Films that presented the best efficiency on reduction of microbial growth as well as best permeability and mechanical properties were: (i) MCS/GEL and (ii) GLU/GEL, both with 2% of added PS. The active films selected for the diffusion halo assay presented two loss tangent (tan?) values, an indication of two Tgs. GLU/GEL films, with no sorbate and with 2% sorbate, were used in sliced bread packaging. Each slice was placed between two sheets of active film and the whole bread was stored inside a low density polyethylene bag. The active films promoted an increase in firmness and a decrease in both moisture content and water activity of the slices. The microbial analysis, storage with active films showed no significant difference from the control sample. By the seventh day of storage the accumulated amout of, potassium sorbate liberated by the film achieved the limit set by Brazilian legislation / Doutorado / Doutor em Tecnologia de Alimentos
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/256345 |
Date | 25 November 2008 |
Creators | Bertan, Larissa Canhadas |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Kieckbusch, Theo Guenter, 1942-, Collares-Queiroz, Fernanda Paula, 1966-, Mei, Lúcia Helena Innocentini, Palmu, Patricia Sayuri Tanada |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia de Alimentos, Programa de Pós-Graduação em Tecnologia de Alimentos |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 203 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds