In this thesis complexes of acylchalcogoureas with cadmium (II), lead (II) and nickel (II) have been synthesised and investigated as single source precursors for the formation of metal chalcogenide thin films viaaerosol assisted chemical vapour deposition (AACVD). Routes to binary thin films have been explored using homoleptic complexes of the general structure bis(N,N-diethyl-N'-naphthoylchalcogoureato)metal(II). Analysis of the thin films produced showed the successful deposition of the binary materials from the synthesised complexes when characterised by powder XRD, ICP-OES, SEM and EDX. Routes to ternary thin films with the general structure MExE'1-x, where M represents a metal (Cd, Ni and Pb); and E chalcogen (S or Se) have been investigated using heteroleptic metal complexes of cadmium, nickel or lead including different chalcogen containing N,N-diethyl-N'-naphthoylchalcogoureato ligands and diethyldithiocarbamate. The precursors were fully characterised and novel compounds had their crystal structures determined. The heteroleptic complexes were thermolysed by AACVD forming the MExE'1-x thin films. In the cases of lead, nickel and cadmium the thin films produced showed that the composition of the film tended heavily towards the metal selenide. Ternary films of type MS1-xSex was prepared by mixing their binary precursors of type bis(N,N-diethyl-N'-naphthoylselenoureato)metal(II) and bis(N,N-diethyl-N'-naphthoylthioureato)metal(II) [metal = Cd, Ni and Pb]. In the case of lead and cadmium chalcogenide films variation of the ratio of sulphur and selenium containing precursors allowed for the full transition in composition between metal sulphide and metal selenide. In the case of CdS1-xSexthe band gap of the films was determined from UV-visible spectroscopy to vary from 2.4 eV (CdS) to 1.7 eV(CdSe). In the case of NiS1-xSex the movement from sulphide to selenide was less simple with multiple phases of nickel chalcogenides produced.

Identiferoai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:727876
Date January 2016
CreatorsEzenwa, Emmanuel
PublisherUniversity of Manchester
Source SetsEthos UK
Detected LanguageEnglish
TypeElectronic Thesis or Dissertation
Sourcehttps://www.research.manchester.ac.uk/portal/en/theses/nndiethylnnaphthoylacylchalcogoureatometal-iicomplexes-as-precursors-for-ternary-metal-chalcogenide-thin-films-via-aacvd(85420a4c-89d4-4465-9734-ca40a75ba924).html

Page generated in 0.0021 seconds