Metal alloy honeycomb structures were fabricated using a paste extrusion technique and characterized for potential application as interconnects in solid oxide fuel cells. Thermal expansion characteristics of Fe-Cr, Fe-Ni, Ni-Cr, Fe-Ni-Cr, and similar alloys containing an oxide dispersion were determined and compared with the thermal expansion behavior of yttria-stabilized zirconia (YSZ). A method was developed to calculate thermal expansion mismatch between two materials under a variety of heating and cooling conditions. It was shown that Fe 20 wt% Cr and Fe 47.5 wt% Ni alloys have low expansion mismatch with YSZ under a wide range of heating and cooling conditions. Oxidation experiments showed that Fe-Cr alloys have superior oxidation resistance in air at 700℃compared with Fe-Ni-Cr alloys with similar chromium contents. The inclusion of oxide dispersions (Y₂O₃ and CaO) into an alloy honeycomb was shown to improve oxidation resistance without affecting thermal expansion behavior. The honeycomb extrusion process provides a method by which experimental alloys can be produced and characterized rapidly to develop an alloy suitable for use as an interconnect in a solid oxide fuel cell.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/4829 |
| Date | 03 November 2004 |
| Creators | Church, Benjamin Cortright |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Language | en_US |
| Detected Language | English |
| Type | Dissertation |
| Format | 6523913 bytes, application/pdf |
Page generated in 0.0017 seconds