Polypropylen s řízenou dobou života / Controlled life-time polypropylene

The master´s thesis is focused on the characterization of degradation process of polypropylene and polypropylene with statistic copolymer into which manganese (II) stearate and cobalt (II) stearates were added at 0.05, 0.10 and 0.20 wt.% loadings. The aim of the thesis was to prepare the controlled life-time polypropylene. The degradation was studied at varying temperatures and prodegradant loadings. The prodegradants were synthetized and characterized using the FTIR and DSC techniques. Thermooxidation of the tested samples induced the changes in crystallinity, melting points and melt-flow indexes. Tensile strength and other mechanical properties were determined by means of the tensile test. The carbonyl index was determined using FTIR, the thermooxidation stability test was used to determine the activation energies of reactions. The changes in morphology of degraded samples were observed by SEM analysis.

Identiferoai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:295673
Date January 2017
CreatorsDemková, Eva
ContributorsPetruš, Josef, Tocháček, Jiří
PublisherVysoké učení technické v Brně. Fakulta chemická
Source SetsCzech ETDs
LanguageSlovak
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/masterThesis
Rightsinfo:eu-repo/semantics/restrictedAccess

Page generated in 0.0021 seconds