Previous issue date: 2017-07-13 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Este trabalho consiste na investigação das propriedades estruturais, magnéticas e ópticas de filmes finos de óxido de cobre (CUQO) dopados com íons de manganês, obtidos pela técnica de eletrodeposição . O óxido de cobre se apresenta em duas fases, 0 CugO e o 0110, sendo que o processo de transição entre elas se da pelo simples tratamento térmico, realizado em ambiente rico em oxigênio. Esta é uma das grandes qualidades deste material, pois por um processo simplório é possível obter filmes com propriedades bastante distintas e interessantes para aplicações tecnológicas em células solares, catalisadores, dentre outros. O trabalho foi divido em duas etapas: primeiro investigou-se o processo de deposição dos filmes por meio da técnica de eletrodeposição. Esta etapa foi necessária Visto que a eletrodeposição não é uma técnica bem estabelecida para a síntese de DMSºs. Sendo assim, foi necessário um estudo para determinar a concentração de sulfato de manganês a ser utilizado ao longo do trabalho, além de determinar os melhores parâmetros de eletrodeposição para a obtenção de filmes de boa qualidade. No fim deste processo chegou-se ao eletrólito a ser utilizado, este contêm: 0,4M CuSO4 (sulfato de cobre), 3,oM 03H603 (ácido lático) e 0,015M M 77,804 (sulfato de manganês), além de 5, oM de hidróxido de sódio para manter o pH da solução em 9. O substrato utilizado foi silício do tipo - n (100), a deposição foi realizada em duas condições de temperatura: valor ambiente e a 6000. Os filmes foram obtidos em diferentes potenciais de deposição: -0, 60, -0, 65, -0, 70 e -0, 75 V vs. SCE, sendo que em todos eles foram possíveis se obter filmes na estequiometria CugO. Por fim, estes passaram por um processo de tratamento térmico, durante uma hora sob a temperatura de 40000 com forno aberto proporcionando a mudança para a fase CuO. A segunda etapa do trabalho consiste na caracterização dos filmes obtidos. Esta foi conduzida através de difratometria de raios X, espectroscopia Raman, espectroscopia de absorção UV-Vis, espectroscopia de foto- luminescência (PL) e espectroscopia de ressonância paramagnêtica(EPR). Os resultados obtidos por difratometria de raios X mostraram que os filmes finos de 011,20 eletrodepositados e sem tratamento térmico apresentam uma orientação preferencial na direção (111), enquanto que após o tratamento térmico a composição dos filmes é alterada, sendo a fase CuO predominante. A espectroscopia Raman confirmou a mudança na estrutura do depósito, e também confirmou a não existência de compostos derivados do manganês. Os resultados de EPR mostraram que os filmes contêm íons de cobre intersticiais em sua estrutura e não mostraram sinais correspondentes ao manganês. A espectroscopia de fotoluminescência exibiu as emissões excitônicas atribuídas ao óxido de cobre em suas duas principais fases. Sendo assim, os resultados confirmam a mudança de fase do óxido de cobre ao passar pelo tratamento térmico em condições de temperatura e pressão ambiente. Porém, não foram obtidos resultados concretos a respeito da dopagem e da concentração de manganês nos filmes. / This work consists in an investigation the structural, magnetic and Optical properties of copper oxide (CagO) thin films doped with manganese ions, obtained by electrodeposition technique. Copper oxide occurs naturally in two abundant phases, 011,20 and 0110, and the transition process between them can be performed easily by thermal treatment at ambient pressure under oxygen-rich conditions. This characteristic is one of the great advantages of this material, because by a simple process it is possible to obtain films with very different prOperties and with a great interest for technical applications in solar cells, catalysts, among others. The electrodeposition is not a very well established technique for the production of dilute magnetic semiconductors. Therefore, a study was needed to determine the concentration of manganese sulphate to be used throughout the work, in addition to determining the best electrodeposition parameters to obtain good quality films. At the end of this process we reached the electrolyte to be used, it contains: O, 4 M CuSO4 (copper sulfate), 3, O M 03H603 (lactic acid) and 0,015 M M nSO4(manganese sulfate), in addition to 5,0 M of sodium hydroxide to maintain the pH of the solution at around 9. The substrate used was the silicon with n-type doping (100), the deposition was performed at room temperature and also at 6000. The films were obtained at different deposition potentials: -O,60, -O,65, -O, 70 and -0, 75 V vs SCE, in all of them it was possible to obtain films in the CUQO stoichiometry. Finally, they underwent a thermal treatment process, during one hour under the temperature of 40000 with Open oven enabling the CuO phase. The second stage of the work consists of the characterization of the obtained films. This was conducted by X-ray diffractometry, Raman spectroscopy, UV-Vis absorption spectroscopy, paramagnetic resonance spectroscopy(EPR) and photoluminescence (PL) spectroscopy. The results obtained by X - ray diffractometry showed that the thin films of CagO electrodeposited and without thermal treatment have a preferential orientation in the direction (111), while after the thermal treatment the composition of the films was changed, with the CuO phase being predominant. Raman spectroscopy confirmed the change in deposit structure, and also confirmed the non-existence of compounds derived from manganese. The EPR results showed that the films contain intertitial copper ions in their structure and showed no signals corresponding to manganese. Photoluminescence spectroscopy exhibited the excitonic emissions attributed to copper oxide in its two main phases. Thus, the results confirm the phase change of the copper oxide when undergoing the thermal treatment under conditions of temperature and ambient pressure. However, no concrete results were obtained regarding dOping and manganese concentration in the films.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:123456789/18269 |
Date | 13 July 2017 |
Creators | Miranda, Ana Paula |
Contributors | Araujo, Clodoaldo Irineu Levartoski de, Felix, Jorlandio Francisco |
Publisher | Universidade Federal de Viçosa |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFV, instname:Universidade Federal de Viçosa, instacron:UFV |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0205 seconds