Obtenção e caracterização de compósitos de poliestireno pós-consumo reforçado com celulose de bagaço de cana-de-açúcar

Dissertação (mestrado)—Universidade de Brasília, Faculdade Gama, Faculdade de Tecnologia, Programa de Pós-Graduação em Integridade de Materiais da Engenharia, 2014. / Submitted by Raquel Viana (raquelviana@bce.unb.br) on 2014-10-27T15:29:24Z
No. of bitstreams: 1
2014_LuizCarlosCorreiadeJesus.pdf: 4417231 bytes, checksum: b867ed85ae8333825735a811f93f749c (MD5) / Approved for entry into archive by Raquel Viana(raquelviana@bce.unb.br) on 2014-10-29T15:41:57Z (GMT) No. of bitstreams: 1
2014_LuizCarlosCorreiadeJesus.pdf: 4417231 bytes, checksum: b867ed85ae8333825735a811f93f749c (MD5) / Made available in DSpace on 2014-10-29T15:41:57Z (GMT). No. of bitstreams: 1
2014_LuizCarlosCorreiadeJesus.pdf: 4417231 bytes, checksum: b867ed85ae8333825735a811f93f749c (MD5) / O EPS (poliestireno expandido) é um polímero resultante da polimerização do estireno em água e é imensamente utilizado para a confecção de embalagens. O produto final é composto por pérolas de até três milímetros de diâmetro que se destinam à expansão com vapor quente. Na natureza, este polímero pode levar vários anos para ser degradado. Pensou-se neste trabalho testar a viabilidade de reforçar o PS com fibras naturais a fim de aliar as propriedades das fibras com a versatilidade do polímero. Deste modo, o principal objetivo deste trabalho é avaliar as propriedades mecânicas, térmicas, reológicas e morfológica dos compósitos de poliestireno (PS) reciclado reforçado com fibra de celulose de bagaço de cana-de-açúcar com lignina residual. Além de avaliar o perfil da lignina com agente compatibilizante, verificando a interface entre fibra de celulose e a matriz do poliestireno. Para a obtenção das fibras celulósicas, a extração foi realizada pelo processo de polpação em meio fortemente alcalino (NaOH). Os compósitos foram obtidos por extrusão em extrusora mono-rosca e posteriormente em dupla-rosca, e depois injetados. Os materiais foram caracterizados por ensaios mecânicos, análises térmicas (TGA, HDT, DSC e DMA), análise reológica (reometria de placas paralelas e índice de fluidez), microscopia (MEV) e FTIR/ATR. Os resultados obtidos demonstram que a adição de fibra de celulose fez com que a resistência à flexão e tração e os módulos aumentassem e concomitantemente a dureza. Com relação às análises térmicas, estas técnicas permitiram a avaliação do limite de temperatura no qual este material pode ser processado, como também a influência do teor de fibras na matriz e a temperatura de deflexão térmica. As curvas de TGA mostraram que os compósitos tem uma estabilidade térmica intermediária entre fibra de celulose e matriz polimérica e o DSC para os compósitos mostraram eventos térmicos semelhantes em relação ao PS reciclado. O HDT mostrou que quando é adicionada fibra na matriz polimérica, a temperatura de deflexão também é aumentada. As curvas DMA mostraram aumento do módulo de armazenamento do polímero e dos compósitos e a Tg (temperatura de transição vítrea) em relação aos dados da literatura. A análise da microestrutura por MEV do PS e dos compósitos permitiram avaliar os mecanismos de falha dos compósitos, mostrando a razoável transferência de tensão entre fibra e matriz antes do rompimento do material. Os ensaios reológicos confirmaram a relação entre massa molar, viscosidade e índice de fluidez. O compósito que apresentou o menor IF e maior viscosidade foi o com 20% de fibra de celulose, portanto, este apresenta a maior massa molar viscosimétrica. Desta maneira, foi possível definir a melhor forma de processamento, desempenho mecânico, limites de temperatura de aplicação e processamento, estabilidade térmica, interface entre fibra e matriz, viscosidade, massa molar e índice de fluidez para os compósitos de PS reforçados com celulose de bagaço-de-cana. ______________________________________________________________________________ ABSTRACT / The EPS (expanded polystyrene) is a polymer resulting from the polymerization of styrene in water and is greatly used in package manufacturing. The final product consists on the three millimeters diameter spheres expansion with hot steam. In nature, this polymer can take several years to be degraded. Thus, the main objective of this work is to evaluate the mechanical, thermal, rheological and morphological properties of composites of polystyrene (PS) reinforced with recycled cellulose fiber bagasse sugarcane residual lignin. In addition to evaluating the profile of lignin with coupling agent, verifying the interface between cellulose fiber and polystyrene matrix.To obtain cellulosic fibers, the extraction was performed by the pulping process in strongly alkaline medium (NaOH). The composites were extruded in single-screw extruders, following by twin-screw and then submitted to injection molding. The materials were characterized by mechanical testing, thermal analysis (TGA, HDT, DSC and DMA), rheological analysis (rheometry parallel plate and melt flow index test), microscopy (SEM) and FTIR/ ATR . The results showed that the addition of cellulose fibers contributes to tensile, flexural strength and modules and hardness increasing. Regarding the thermal analyzes, these techniques permitted the evaluation of the temperature at which this material could be processed, and the influence of the matrix fiber content in heat deflection temperature. The TGA curve showed that the composite has a thermal stability intermediate between the cellulose fiber and polymer matrix. DSC showed similar thermal events in respect to recycled PS. HDT showed that when the fiber is added into the polymer matrix, the deflection temperature is also increased. The DMA curves showed an increase in the storage modulus and Tg (glass transition temperature) of the polymer and composites compared to literature. The microstructural analysis by SEM for PS and composites allows assessing the failure mechanisms of composites, showing a reasonable transfer of tension between fiber and matrix before the rupture of the material. However the FTIR did not confirm this observations regarding adhesion between fiber and matrix. The rheological tests confirmed the relationship between molar mass, viscosity and melt flow index. The composite with the lowest IF and the viscosity was increased with 20% cellulose fiber, so this has the highest viscosimetric molar mass. Thus, it was possible to define the best way of processing, mechanical performance, application and processing temperature limits, thermal stability, interface between fiber and matrix, viscosity, molecular weight and melt index for the PS composites reinforced with cellulose from sugarcane bagasse.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/16651
Date24 March 2014
CreatorsJesus, Luiz Carlos Correia de
ContributorsLuz, Sandra Maria da
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB
RightsA concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds