Orientador: Mário Alexandre Coelho Sinhoreti / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T06:42:26Z (GMT). No. of bitstreams: 1
Vitti_RafaelPino_D.pdf: 971338 bytes, checksum: 04747212bf9b8bde6e4a37081ac788e6 (MD5)
Previous issue date: 2013 / Resumo: Os objetivos neste trabalho foram (1) avaliar e comparar propriedades físico-químicas de cimentos endodônticos, sendo um recentemente desenvolvido à base de mineral trióxido agregado (MTA Fillapex, Angelus, Londrina, Brasil) e outro à base de resina epóxica (AH Plus, Dentsply, Konstanz, Alemanha); e (2) desenvolver e avaliar propriedades físico-químicas de três cimentos endodônticos experimentais à base de MTA e uma resina de salicilato com diferentes fosfatos de cálcio (CaP). Os materiais foram manipulados de acordo com as instruções dos fabricantes. Os cimentos experimentais foram compostos de pastas bases e catalisadoras misturadas em 1:1. A pasta base foi composta de 60% de óxido de bismuto e 40% de butilenoglicol dissalicilato. Três diferentes pastas catalisadoras foram formuladas contendo: (1) 60% de MTA, 39% de Resimpol 8 e 1% de dióxido de titânio; (2) 40% de MTA, 39% de Resimpol 8, 20% de hidroxiapatita e 1% de dióxido de titânio e; (3) 40% de MTA, 39% de Resimpol 8, 20% de fosfato dibásico de cálcio diidratado e 1% de dióxido de titânio. MTA Fillapex foi usado como controle. O tempo de trabalho e escoamento foi testado de acordo com a ISO 6876:2001 e o tempo de presa de acordo com a ASTM C266 (n=3 para cada material e teste). Os materiais foram colocados em moldes de PVC (8 mm x 1,6 mm) e armazenados em recipientes contendo 20 ml (testes de solubilidade e absorção de água) ou 10 ml (ensaios de pH e liberação de cálcio) de água deionizada a 37ºC (n=10 para cada material e teste). Em 1, 7, 14 e 28 dias as amostras foram removidas dos recipientes e secas para aferiação da solubilidade e absorção de água. Após 3 e 24 horas e 4, 7, 14 e 28 dias, a água dos recipientes foi coletada para análises do pH e liberação de cálcio. Os dados foram analizados usando ANOVA um fator e teste de Tukey (5%). MTA Fillapex mostrou menores valores de escoamento e tempos de trabalho e presa em relação ao AH Plus (p<0,05). MTA Fillapex obteve os maiores valores de escoamento e tempos de trabalho e presa em comparação aos materiais experimentais (p<0,05). MTA Fillapex apresentou os menores valores de solubilidade e absorção de água (p<0,05). Todos os cimentos experimentais e o MTA Fillapex apresentaram pH básico e liberação de íons cálcio. MTA Fillapex e AH Plus mostraram valores de acordo com a ISO 6876:2001. Os materiais experimentais apresentaram propriedades físico-químicas satisfatórias / Abstract: The aims of this study were (1) to evaluate and to compare physicochemical properties of endodontic sealers, a recent calcium-silicate based sealer (MTA Fillapex, Angelus, Londrina, Brazil) and other an epoxy resin based sealer (AH Plus, Dentsply, Konstanz, Germany); and (2) to develop and to evaluate physicochemical properties of three experimental root canal sealers made by mineral trioxide aggregate (MTA) and a salicylate resin with different calcium phosphates (CaP). The materials were handled following the manufacturer's instructions. The experimental materials were composed of a base and a catalyst pastes mixed in a 1:1. The base paste was made by 60% bismuth oxide and 40% butyl ethylene glycol disalicylate. Three different catalyst pastes were formulated with: (1) 60% MTA, 39% Resimpol 8 and 1% titanium dioxide; (2) 40% MTA, 39% Resimpol 8, 20% hydroxyapatite and 1% titanium dioxide and; (3) 40% MTA, 39% Resimpol 8, 20% dibasic calcium phosphate dihydrate and 1% titanium dioxide. MTA Fillapex was used as control. The working time and flow were tested according to ISO 6876:2001 and the setting time according to ASTM C266 (n=3 for each material and test). The materials were placed into PVC molds (8 mm x 1.6 mm) and stored in containers with 20 mL (solubility and water absorption tests) or 10 mL (calcium release and hydroxyl ions tests) of deionized water at 37°C (n=10 for each material and test). At 1, 7, 14 and 28 days the samples were removed from the solutions and dry for solubility and water absorption tests. After 3 and 24 h and 4, 7, 14, 28 days the soaking water was collected for Ca and pH analysis. The data were analyzed using one-way ANOVA with Tukey's test (5%). MTA Fillapex showed lower values of flow and working and setting times when compared to AH Plus (p<.05). MTA Fillapex had the higher values of flow and working and setting times when compared to experimental materials (p<.05). MTA Fillapex presented the lowest values of solubility and water absorption (p<.05). All experimental cements and MTA Fillapex showed basifying activity and released calcium ions. MTA Fillapex and AH Plus showed values in according to the ISO 6876:2001. The experimental materials showed satisfactory physicochemical properties / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288133 |
| Date | 22 August 2018 |
| Creators | Vitti, Rafael Pino, 1984- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Sinhoreti, Mário Alexandre Coelho, 1969-, Lopes, Murilo Baena, Zanchi, Cesar Henrique, Goes, Mario Fernando de, Ferraz, Caio Cezar Randi |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Multilíngua |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 53 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds