Previous studies have shown that pullulan films are able to stabilize enzymes and other labile molecules from thermal and oxidative degradation. Solutions made with commercially available pullulan are extremely viscous and difficult to process limiting the ability to use low-cost printing systems, such as inkjet printers, to format pullulan-containing. In this work, we show that pullulan can be made printable by decreasing its chain length by acid hydrolysis. The acid hydrolysis reaction was modelled using statistical software; the molecular weight of pullulan decreased with increasing reaction time, temperature and acid concentration. Interactions between time and temperature, and temperature and acid concentration were determined to be significant to the reaction as well.
The mechanical properties and oxygen permeability of films made from pullulan with different molecular weights were also measured. The films were found to have similar tensile properties and oxygen permeabilities to each other and to those obtained using native pullulan. Using a thermally unstable enzyme (acetylcholinesterase) and an easily oxidizable small molecule (indoxyl acetate) as test materials, it was found that these films have the same ability to stabilize the enzyme and to serve as an oxygen barrier, as the films made with native pullulan.
It was also found that pullulan is inkjet printable as long as the molecular weight is 56 kDa. Poor jetting and clogging of the printhead was observed when pullulan with a molecular weight higher than this threshold was used. Microarray printing was also demonstrated by a printing acetylcholinesterase/pullulan in nano-sized volumes using a Dimatix inkjet printer and showing activity of the enzyme after printing and storage at ambient conditions. Proof of concept of microarray printing opens up the potential for future applications of pullulan in other high throughput applications. / Thesis / Master of Applied Science (MASc)
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/20538 |
| Date | January 2016 |
| Creators | Ng, Robin |
| Contributors | Filipe, Carlos, Chemical Engineering |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Thesis |