Investigation of the quench and heating rate sensitivities of selected 7000 series aluminum alloys

"The quench sensitivity of AA7136 has been experimentally investigated using Jominy end quench and test coupons of various heat treatments. It was found that this alloy is not quench sensitive. In addition, the effects of heating rate on both solution and aging treatments on AA7136 and AA7075 were determined using a newly developed reverse Jominy heating test. It was observed that hardness was reduced after rapid heating during aging and hardness increased slightly after rapid heating during solutionizing. These results are discussed in terms of microstructural developments. "

Identiferoai:union.ndltd.org:wpi.edu/oai:digitalcommons.wpi.edu:etd-theses-1932
Date13 August 2007
CreatorsNowill, Courtney Ann
ContributorsRichard D. Sisson, Jr., Advisor, Mohammed Maniruzzaman, Committee Member, Diran Apelian, Committee Member
PublisherDigital WPI
Source SetsWorcester Polytechnic Institute
Detected LanguageEnglish
Typetext
Formatapplication/pdf
SourceMasters Theses (All Theses, All Years)

Page generated in 0.0016 seconds