CoordenaÃÃo de AperfeiÃoamento de Pessoal de NÃvel Superior / Com o rÃpido crescimento de tecnologias sem fio, a indÃstria de telecomunicaÃÃes tem buscado constantemente materiais que possuam excelentes caracterÃsticas dielÃtricas para ser à base de novos dispositivos. Devido a essa demanda sempre crescente, pesquisas em busca de novos e melhores materiais cerÃmicos tÃm ocupado cada vez mais lugar de destaque no interesse da comunidade cientÃfica mundial. O uso de materiais cerÃmicos em busca de materiais fluorescentes tambÃm vem recebendo destaque, jà que materiais desse tipo apresentam diversas aplicaÃÃes, tais como lasers; diodo emissor de luz (LED); como fonte de luz sensores; estocagem de dados Ãticos e atà mesmo na Ãrea mÃdica. Neste trabalho foram estudados as propriedades da matriz cerÃmica LaNbO4 (LNO) modificada pela adiÃÃo de ZnO e tambÃm pela dopagem com Ãons terras-raras Ãrbio; itÃrbio e tÃlio. As amostras de LNO e dopadas foram obtidas atravÃs do mÃtodo reacional do estado sÃlido utilizando Ãxidos precursores seguido de tratamento tÃrmico, enquanto as amostras com ZnO foram obtidas atravÃs da adiÃÃo de determinada quantidade de massa deste sobre o LNO. Os resultados de difraÃÃo de Raios-X e espectroscopia Raman confirmaram a obtenÃÃo da fase cerÃmica LNO e os valores das propriedades dielÃtricas desse material foram prÃximos da literatura. A simulaÃÃo numÃrica realizada para o LNO apresentou bom valor de ganho e alta eficiÃncia, mostrando que esse material pode atuar como DRA. Quanto à adiÃÃo de ZnO, a difraÃÃo de Raios-X mostrou que praticamente nÃo houve mudanÃas no padrÃo de difraÃÃo da fase LNO. Jà com relaÃÃo Ãs propriedades dielÃtricas foi observado que essa adiÃÃo causou aumento nos valores de permissividade e tangente de perda de forma nÃo linear com o aumento da concentraÃÃo de zinco. Nos sistemas contendo Ãons terras-raras a difraÃÃo Raios-X e espectroscopia Raman indicaram que os Ãons dopantes entraram na estrutura cristalina da fase LNO. Na fluorescÃncia foram observadas bandas na regiÃo do verde e vermelho para as amostras com Er3+ e Yb3+, referentes Ãs transiÃÃes dos orbitais 4f do Er3+. Enquanto que para o sistema com Er3+, Yb3+ e Tm3+ foram observadas bandas nas regiÃes do ultra-violeta; azul; verde; vermelho e infravermelho originadas das transiÃÃes dos orbitais 4f do Er3+ e 4f do Tm3+. / With the rapid growth of wireless technologies, the telecommunications industry has
constantly searching materials having excellent dielectric characteristics to be based on new
devices. Due to this ever increasing demand, research for new and improved ceramic
materials have occupied prominent place in the interest of the scientific community
worldwide. The use of ceramic materials in search of fluorescent materials also has received
attention, since such materials have several applications, such as lasers; light emitting diode
(LED); as a source of light sensors; optical data storage and even in the medical field. In this
work were studied the properties of LaNbO4 (LNO) matrix modified by adding of ZnO and
also by doping with rare-earth ions erbium; ytterbium and thulium. The pure and doped
LaNO4 samples were obtained by solid state reaction method using oxide precursor followed
by heat treatment, while samples with ZnO was obtained by adding of determined quantity of
latter on the LNO. The results of x-ray diffraction and Raman spectroscopy confirmed the
formation of the ceramic phase LNO and the values of the dielectric properties obtained of
this material were close to the values of the literature. The numerical simulation realized for
LNO presented good gain value and a high efficiency, showing that this material can act as a
DRA. About the addition of zinc, the x-ray diffraction showed that practically not occured
significant changes in the diffraction pattern of LNO phase, being that regarding the dielectric
properties was observed that the addition caused increase in the values of the permittivity and
loss tangent nonlinearly with the increasing of the concentration of zinc. In the systems
containing rare-earth ions the X-ray diffraction and Raman spectroscopy indicated that the
dopant ions entered on the crystalline lattice of LNO phase. In the fluorescence were observed
bands in the green and red region for the system with Er3+ and Yb3+
, concerning the
transitions between the 4f orbitals of Er3+
. While for the system with Er3+
, Yb3+ and Tm3+ were
observed bands in the ultraviolet region; blue; green; red and infrared originated of transitions
that occur in the 4f orbitals of Er3 +
and in the 4f orbitals of Tm3+.
| Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:8656 |
| Date | 17 July 2014 |
| Creators | JoÃo Paulo Costa do Nascimento |
| Contributors | AntÃnio SÃrgio Bezerra Sombra, Francisco Nivaldo Aguiar Freire, Adonay Rodrigues Loiola |
| Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em QuÃmica, UFC, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0013 seconds