This research took place in 3 stages. In the first stage, lignin graphene (LG) was synthesized using a catalytic thermal conversion process. In stage 2, the time and temperature correlations for polyvinyl acetate (PVAc) and phenol resorcinol formaldehyde (PRF) adhesives were found and PRF showed stronger correlation when doped with carbon nanomaterials. Stage 3 evaluated the effect of the nanomaterials on radio frequency (RF) heating time and adhesive strength. It was found that all versions of the PRF adhesive resulted in higher shear strength values when cured in room temperature for 24 hours or in an oven at 170 °F for 30 minutes. The combination of PRF + 0.5 % LG and 120 s RF heating resulted in significantly higher block shear strengths when compared to the other RF heating durations.
Pine lumber was selected as it is the single most important commercial/structural species in North America, by volume. A substantial portion of pine is directed to glue-laminated timber and cross-laminated timber. Both industries use or can use RF curing and as such both may benefit from improvements developed herein.
| Identifer | oai:union.ndltd.org:MSSTATE/oai:scholarsjunction.msstate.edu:td-6904 |
| Date | 08 August 2023 |
| Creators | Henfield, Bradia T. |
| Publisher | Scholars Junction |
| Source Sets | Mississippi State University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
Page generated in 0.0014 seconds