Produção e caracterização de nanopartículas de quartzo obtidas por moagem e separação granulométrica de solução aquosa / Production and characterization of quartz nanoparticles obtained by ball milling process and granulometric seperations from water solution

Orientador: Carlos Kenichi Suzuki / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-27T06:45:12Z (GMT). No. of bitstreams: 1
Schenkel_EgontAlexandre_M.pdf: 11831501 bytes, checksum: 100fb5f4a5379818f466b361ab913849 (MD5)
Previous issue date: 2015 / Resumo: Neste trabalho foi apresentada uma metodologia para obtenção de nanocristais de quartzo a partir do processo de moagem em moinho de bolas rotativas, com posterior separação granulométrica lançando mão da decantação de partículas de maior densidade em meio aquoso. Foram estudadas duas fontes de quartzo natural com diferentes origens geológicas, uma proveniente de Soledade-PB e outra de Belmonte-BA. Esses minerais foram processados e seu produto foi caracterizado utilizando técnicas de difração de raios-X (DRX) e microscopia eletrônica de varredura (MEV). Como resultado, foram obtidas nanopartículas com morfologia irregular, com parcial perda de cristalinidade e tamanho médio em torno de 100 nm. Foram também efetuados testes de obtenção desse material em escala industrial. Como resultado, foram obtidas partículas de quartzo submicrométricas (~300 nm) com propriedades estruturais similares às obtidas em laboratório / Abstract: This work presents a methodology to obtaining quartz nanocrystals from the ball milling and granulometric particle separation in an aqueous solution. Two sources of natural quartz were studied with different geological origins, one from Soledad-PB and another of Belmonte-BA. These minerals were processed and their product was characterized using X-Ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. As a result, nanoparticles were obtained with irregular morphology, partial loss of crystallinity and average size around 100 nm. Tests have also been made to obtain this material on industrial scale. As a result, submicron quartz particles were obtained (~ 300 nm) with similar structural properties to those obtained in the laboratory / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265809
Date03 November 2015
CreatorsSchenkel, Egont Alexandre, 1982-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Suzuki, Carlos Kenichi, 1945-, Mei, Paulo Roberto, Torikai, Delson
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format48 f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0023 seconds