For high-resolution X-ray imaging scintillator applications, we have prepared and optically characterized divalent samarium doped fluorochlorozirconate (FCZ:Sm2+) glasses and glass-ceramics. Sm2+ doped FCZ glasses were obtained by adding a reducing agent, NaBH4 into the initial melt to convert some of the Sm3+ to Sm2+. However, the Sm2+ concentration at most was estimated to be only approximately 0.003 %. The as-prepared glass samples were further heat treated to obtain glass-ceramics; the nucleation and growth of BaCl2 nanocrystals were confirmed by powdered X-ray diffraction (XRD) experiments. Depending on the heat treatment conditions (temperature and time), the average nanocrystal size varies from 8 to 170 nm, and the sample contains BaCl2 nanocrystals with the orthorhombic and/or hexagonal structure. The optical absorption spectra for our glass-ceramic samples suggested the substitution of Sm2+ ions into the BaCl2 lattice site. The FCZ:Sm2+ glass-ceramics samples showed strong fluorescence in the red region of spectrum (approximately 8 times that of an as-prepared glass), and the transparency can be very high (transmittance > 80 % for samples with thickness about 0.5 mm) and can be equivalent to that of an as-prepared glass . These two results promise potential as a high-resolution X-ray scintillator due to the emission wavelength range and high transparency. Extensive studies of photoluminescence (PL) spectra at low temperatures (12 -- 200 K) for FCZ:Sm2+ glass-ceramics suggested useful indicators of the crystal structure and average size of embedded BaCl2 nanocrystals. A detailed analysis of the optical spectra has lead to the identification of the origin of the emission peaks and the location of Sm ions at specific crystallographic sites. X-ray induced luminescence (XL) studies have suggested a strong dependence of the fluorescence intensity on the concentration of Sm2+ ions. In addition, for more efficient fluorescence, a sample should be heat treated in a hydrogen containing atmosphere (e.g. H2 + Ar gas), and the heat treatment conditions should be such that the nanocrystals grow in the hexagonal structure.
Identifer | oai:union.ndltd.org:USASK/oai:usask.ca:etd-06302010-152011 |
Date | 08 July 2010 |
Creators | Okada, Go |
Contributors | Chen, Li, Yang, Qiaoqin, Johanson, Robert, Kasap, Safa |
Publisher | University of Saskatchewan |
Source Sets | University of Saskatchewan Library |
Language | English |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://library.usask.ca/theses/available/etd-06302010-152011/ |
Rights | unrestricted, I hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to University of Saskatchewan or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report. |
Page generated in 0.0022 seconds