Aim of magister´s thesis was to study reaction kinetics of dental materials. Thesis was focused on dimethacrylate dental polymers, which are for example used for dental restoration, tooth repair and creating now teeth. First part of the thesis concentrates on influence of molar ratio on reation kinetics by addition of other monomer to polymer resin. Second part concentrates on influence of addition of additive silica on reaction kinetics of polymerization. Essential variables know as a polymerization ratio, conversion, gel point, glass transition temperature and storage modulus were studied. Firstly, polymerization ratio and conversion were observed by differential scanning calorimetry (DSC). Secondly rheology was observed by photoreometr. Finally, glass transition temperature and storage modulus were observed by dynamic mechanical analysis (DMA). Behaviour changes caused by addion of monomer or filler point out decrease of polymeration ratio and converstion. Same behaviour was observed by short exposure. In order to established network formation, values of gel point increased by higher concentration of monomer or filler. Glass transition temperature and storage modulus measured by DMA were evaluated. Those valuables had variable tendency due to monomer acting like filler at higher concentration. Also contradictory impact of different material conversion and filler concetration was discussed.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:414114 |
| Date | January 2020 |
| Creators | Vaněk, Martin |
| Contributors | Bystřický, Zdeněk, Poláček, Petr |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0115 seconds