A cyclic polarization procedure was designed to evaluate the pitting potentials of high performance stainless steels in synthetic concrete pore water at different chloride concentrations. Cyclic polarization scans were performed on high performance stainless steel reinforcements, S32201, S32305 and S32205. Pitting initiation was observed below the oxygen evolution potential for high chloride concentrations. S32201 and S32304 showed the presence of metastable pitting before reaching its pitting potential. Pitting resistance performance, based on cyclic polarization, was consistent with each material's respective Pitting Resistance Equivalent Number (PREN) value. For S32201 and S32304, pitting potential decreased as the chloride concentration increased, whereas S32205 did not pit at the chloride concentrations tested. / by Erika Maria Sanchez. / Thesis (M.S.C.S.)--Florida Atlantic University, 2011. / Includes bibliography. / Electronic reproduction. Boca Raton, Fla., 2011. Mode of access: World Wide Web.
Identifer | oai:union.ndltd.org:fau.edu/oai:fau.digital.flvc.org:fau_3817 |
Contributors | Sanchez, Erika Maria., College of Engineering and Computer Science, Department of Ocean and Mechanical Engineering |
Publisher | Florida Atlantic University |
Source Sets | Florida Atlantic University |
Language | English |
Detected Language | English |
Type | Text, Electronic Thesis or Dissertation |
Format | xiv, 71p. : ill. (some col.), electronic |
Rights | http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.0012 seconds