Orientadores: Saide Sarckis Domitti, Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T01:30:57Z (GMT). No. of bitstreams: 1
Tanji_Mauricio_M.pdf: 3213490 bytes, checksum: a4c59df5e90cc9828835588aa5d0cd4a (MD5)
Previous issue date: 2000 / Resumo: Este trabalho comparou a influência das variáveis resistência ao impacto, dureza de superficie, rugosidade e porosidade em 30 corpos-de-prova de resinas acrílicas termopolimerizáveis Clássico, QC-20 e Onda-Cryl, confeccionados a partir de modelos retangulares de alumínio (65xlO e 64x9 x 3,0 mm), fixados com adesivo instantâneo (Super Bonder, Loctite) em suporte de madeira. Os modelos foram moldados com silicona por condensação para uso laboratorial (Zetalabor-Labordental Ltda.) e os moldes incluídos em muflas metálicas e de fibra de vidro. A proporção póllíquido e mistura, assim como a prensagem das resinas acrílicas foram realizadas de acordo com as instruções dos fabricantes. Após a polimerização nos ciclos de água aquecida a 74°C por 9 horas, água em ebulição por 20 minutos, e por energia de microondas a 1400 W por 3 minutos, os corpos de-prova foram removidos das muflas após esftiamento em temperatura ambiente e submetidos aos processos de acabamento e polimento convencionais. Posteriormente, foram submetidos aos ensaios de resistência ao impacto, numa máquina Otto Wolpert Werke pelo sistema Charpy; de dureza, num microdurômetro Shimadzu (Modelo HMV-2000) calibrado com carga de 25 gramas por 10 segundos; de rugosidade num rugosímetro (Modelo Surfcorder SE 1700); e de porosidade, através da imersão dos corpos-de-prova em tinta Nankin (Acrilex) por 12 horas, lavados em água corrente por 10 segundos, e posteriormente quantificada e fotografada em área previamente determinada. Os resultados submetidos à análise de variância e ao teste de Tukey (5%) mostraram que a porosidade softeu influência dos tipos de resina acrílica com maiores valores para a de microondas, o mesmo ocorrendo para com a dureza. Os menores valores de rugosidade foram mostrados pela resina para microondas, enquanto as demais resinas acrílicas não mostraram diferenças estatisticamente significantes; e a resistência ao impacto não sofreu influência dos tipos de resinas acrílicas / Abstract: This study investigated the influence of the impact strenght, hardness of surface, roughness and porosity variables in 30 specimens on Clássico, QC-20 and Onda-Cryl, thermo-cured acrylic resins. The specimens were made in retangular aluminium mo dei (65xlO and 64x9 x 3,0 mm), attached to a wooden holder by Super Bonder glue (Loctite). The model were printed using a Zetalabor (Labordental Ltda.) silicone for condensation for laboratory purposes and the molds were inc1uded into metal flasks, and reinforced fiberglass flasks. The proportion powder/liquid and mixture, as well as acrylic resin pressing were done following the manufature's instructions. After hot water (74°C) for 9 hours, boiling water for 20 minutes; and microwave energy with 1400W for 3 minutes, curing cyc1es the specimens were removed form flasks after cooling at room temperature and submetted to polishing by conventional procedure. Subsequently, were submetted to impact strenght test by Charpy system in a W olpert machine; and hardness by Shimadzu microdurometer with load of 25 grams during 10 seconds; and the superficial roughness with Surfcorder SE 1700; and porousness by specimens immersion into Nankin ink (Acrilex) for 12 hours, washed into running water for 10 seconds and thererafter the porousness was counted and photographed in pre-determined areas. The results submetted to ANOV A and Tukey's test showed that the porosity was influenced by acrylic resin types with greater values for microwave, the same was showed for the hardness. The roughness and hardness smaller values had been showed for microwave resin, however the other cyc1es didn't show difference statistical significant; and the impact strenght hadn't influence of the acrylic resins types / Mestrado / Protese Dental / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289957 |
| Date | 08 November 2000 |
| Creators | Tanji, Mauricio |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Domitti, Saide Sarckis, 1932-2016, Mesquita, Marcelo Ferraz, Marchese, Marco Polo |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 127p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0032 seconds