Thin films of Strontium Ruthenate have been grown on Strontium Titanate and Lanthanum Aluminate (100) substrates by pulsed laser deposition. X-ray diffraction results show that the films grown on the Strontium Titanate are amorphous and polycrystalline on the Lanthanum Aluminate. Resistances versus temperature measurements show that the films exhibit semiconducting characteristics. In addition to the growth of Strontium Ruthenate thin films, multilayer heterostructures of Terfenol-D thin films on polycrystalline Lead Titanate thin films were grown by pulsed laser deposition. By using a novel experimental technique called magnetic field assisted piezoelectric force microscopy it is possible to investigate the magnetoelectric coupling between the electrostrictive Lead Titanate and magnetostrictive Terfenol-D thin film. Upon examination of the produced thin films the phase and amplitude components of the piezoelectric signal experience changes in response to an applied in-plane magnetic field. These changes provide experimental evidence of a magnetoelectric coupling between the Terfenol-D and Lead Titanate layers.
| Identifer | oai:union.ndltd.org:uno.edu/oai:scholarworks.uno.edu:td-1251 |
| Date | 04 August 2011 |
| Creators | Garza, Ezra |
| Publisher | ScholarWorks@UNO |
| Source Sets | University of New Orleans |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | University of New Orleans Theses and Dissertations |
Page generated in 0.0014 seconds