In this thesis, firstly, carbon-supported platinum nanoparticle catalysts have been prepared by using PtCl4 and H2PtCl6 as starting materials and 1-hexanethiol, and tert-octanethiol, as surfactants for the first time. Secondly, these prepared catalysts were heated to 200 ° / C, 300 ° / C, and 400 ° / C for 4 h under argon gas. Lastly, PtRu/C catalysts, which have different atomic percent ratios of Pt and Ru (Pt/Ru: 0.8, 2.1 and 3.5), were prepared using PtCl4 and RuCl3 as starting materials and tert-octanethiol as a surfactant. Each was characterized by X-ray diffraction, transmission electron microscopy, energy dispersive analysis, X-ray photoelectron spectroscopy, cyclic voltammetry, and elemental analysis, and their activities were determined toward the methanol oxidation reaction. It has been found that all prepared catalysts are more active toward methanol oxidation reaction compared to the commercial catalysts. It was also found that increasing the temperature during the heat treatment process results in an enlargement of platinum particle size and a decrease in catalytic activity in the methanol oxidation reaction. Transmission electron microscopy shows that platinum nanoparticles are homogeneously dispersed on the carbon support and exhibited a narrow size distribution with an average particle size of about 2-3 nm in diameter. X-ray photoelectron spectra of all catalysts indicated that most of the platinum nanoparticles (> / 70 %) have an oxidation state of zero and rest (< / 30 %) have a +4 oxidation state with (Pt 4f7/2) binding energies of 71.2-72.2 and 74.3-75.5 eV, respectively.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12614728/index.pdf |
| Date | 01 September 2012 |
| Creators | Sen, Fatih |
| Contributors | Gokagac, Gulsun |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | Ph.D. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for METU campus |
Page generated in 0.0016 seconds