In this work, a chemiresistor-type sensing platform based on aligned arrays of nitrogen-doped multi-walled carbon nanotubes (N-MWCNTs) was developed. Our N-MWCNT based sensors can be made on both rigid and flexible substrates; they are small, have low power consumption and are suitable for highly efficient and reliable detection of different biomolecules and gases, at room temperature. The performance of these sensors was demonstrated for avian influenza virus (AIV) subtype H5N1 DNA sequences and toxic gases NO and NH3 at low concentrations.
In our study, chemical vapor deposition (CVD) method was applied to synthesize vertically aligned nitrogen doped carbon nanotube arrays on a large area (> 1 cm2) on Si/SiO2 substrate using Fe/Al2O3 layer as a catalyst and a mixture of ethanol and acetonitrile as a C/N source. Especially, the diameter, length, nitrogen-doping concentration and morphology of the nanotubes were controllably tailored by adjusting the thickness of catalyst film, reaction duration and temperature as well as the amount of nitrogen-containing precursor.
For integrating N-MWCNTs into chemiresistor devices, we developed a direct contact printing method for a dry, controllable and uniform transferring and positioning of the CVD-grown vertical nanotubes onto well-defined areas of various rigid and flexible substrates. After horizontally aligned N-MWCNT arrays were formed on a target substrate, interdigitated metallic microelectrodes with an interspacing of 3 µm were deposited perpendicular to the nanotube alignment direction to fabricate chemiresistor devices for biomolecule and gas sensing. This way, well-aligned nanotubes were laid across the Au/Cr interdigitated electrode fingers, had a strong adhesion with the electrodes and served as conducting channels bridging the electrodes.
The N-MWCNT based chemiresistor device was applied as a label-free DNA sensor for a highly sensitive and fast detection of AIV subtype H5N1 DNA sequences. For this, the nanotubes were functionalized with probe DNA, which was non-covalently attached to sidewalls of the N-MWCNTs via π-π interaction. Such functionalized sensors were applied to quantitatively detect complementary DNA target with concentration ranging from 20 pM to 2 nM after 15 min incubation at room temperature. The sensors showed no response to non-complementary DNA target for concentrations up to 2 µM showing an excellent selectivity.
Investigations on the efficient gas sensing of N-MWCNT-based chemiresistor of reducing/ oxidizing gases NH3 and NO were also reported in this work. The aim was to assess the possibility for N-MWCNTs to be applied as innovative sensing materials for room temperature gas sensing. N-MWCNTs with varying doping levels (N/C ratio of 5.6 to 9.3at%) were used as sensing materials and exposed to NH3 (1.5-1000 ppm) and NO (50-1000 ppm) for exploring and comparing their sensing performance. This study offered an effective route for further modification of CNTs according to various sensing application.
Finally, our investigations showed a high potential of the developed N-MWCNT-based sensing platform for various applications ranging from environmental monitoring to point-of-care medical diagnostics.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa.de:bsz:14-qucosa-230524 |
| Date | 10 January 2018 |
| Creators | Fu, Yangxi |
| Contributors | Technische Universität Dresden, Fakultät Maschinenwesen, Prof. Dr. Gianaurelio Cuniberti, Prof. Dr. Gianaurelio Cuniberti, Prof. Dr.-Ing. Thomas Wallmersperger |
| Publisher | Saechsische Landesbibliothek- Staats- und Universitaetsbibliothek Dresden |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | doc-type:doctoralThesis |
| Format | application/pdf |
Page generated in 0.0019 seconds