The final thesis determined the properties of alloys formed from mixtures of powders processed by the SLM method. Powders of alloy AlSi12 and EN AW 2618 were fused in the proportion 75 wt. % AlSi12 + 25 wt. % 2618, 50 wt. % AlSi12 + 50 wt. % 2618 and 25 wt. % AlSi12 + 75 wt. % 2618. Metallographic analysis, EBSD analysis and line EDS microanalysis were made on the samples. Tensile test at room temperature and hardness were carried out to determine the mechanical properties. Fractographic analysis was performed after tensile test.