In this study a presentation of the technology behind dye-sensitized solar cells, their design as well as the role of the different parts of the cell. The characterization of the cell is divided into four sections namely: the characterization of the paste required to make the TiO2 film and its optical properties using SEM-EDX and XRD analytical techniques; Analysis of the various absorptions of three Ru-based dyes using UV-Vis spectroscopy, Photoluminescence and Fourier Transform Infra-Red spectroscopy; the characterization and the analyses of the entire cell using Electrochemical Impedance Spectroscopy. The nine cells were prepared by examining RuL2(CN)2 , RuL2(NCS)2 or N3 dye and RuL2(NCS)2 TBA+ or N719 dye. [L = 2,2'-bipyridyl-4,4'-dicarboxylic acid ;TBA = tetra-butyl ammonium] were combined with three electrolytes namely: Z–150 , AN–50 and PN–50. The Iodolyte PN–50 is an iodide based low viscosity electrolyte with 50 mM of tri-iodide dissolved in a solvent called propionitrile (PN). The Iodolyte AN–50 is an iodide based low viscosity electrolyte with 50 mM of tri-iodide dissolved in a solvent called acetonitrile (AN). The Iodolyte Z–150 is an iodide based low viscosity electrolyte with 150 mM of tri-iodide dissolved in a solvent called 3-methoxypropionitrile (MPN) and with additives such an ionic liquid, malkylbenziimidazole and guanidine thiocyanate. A solar simulator was utilized with which the standard solar irradiation can be created in laboratory conditions. The fill factors as well as overall performance efficiencies of the these cells are quite low < 1.0%,.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:ufh/vital:11341 |
| Date | January 2013 |
| Creators | Caga, Noloyiso |
| Publisher | University of Fort Hare, Faculty of Science & Agriculture |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis, Masters, MSc (Chemistry) |
| Format | 140 leaves; 30 cm, pdf |
| Rights | University of Fort Hare |
Page generated in 0.0065 seconds