Lamellar cast iron is a very important technical alloy and the most used material in the casting production, and especially in the automotive industry which is the major consumer. Beside the many great properties, it is inclined to form casting defects of which some can be prevented, and some may be repaired subsequently. Shrinkage porosity is a randomly returning problem, which is difficult to understand and to avoid. This defect is a volumetric deficiency which appear as cavities inside the casting in connection to the casting surface. Another frequent defect is the metal expansion penetration. This defect is a material surplus squeezed to the casting surface containing sand inclusion from the mold material. Shrinkage porosity is usually mentioned together with metal expansion penetration as the formation mechanism of both defects have common roots. It is also generally agreed, that these type of defects are related to the volumetric changes occurring during solidification. Additionally, the formation of these defects are in connection with the coherency of the primary austenite dendrites. The purpose of this work was to develop knowledge on factors affecting a volume-change related casting defect formation in order to minimize the presence of these defects in engine component production. This was done by extending the existing solidification investigation methods with novel solutions. Introduction of expansion force measurement in the determination of dendrite coherency combined with multi axial volume change measurement refine the interpretation of the solidification. Comparison of registered axial and radial linear deformation in cylindrical samples indicated an anisotropic volume change. Different methods for dendrite coherency determination have been compared. It was shown that the coherency develops over an interval. Dependent on the added inoculant the coherency is reached at different levels of fractions of a solidified primary phase. It is also shown, that inoculation has an effect on the nucleation and growth of the primary phase. Quantitative image analysis has been performed on the primary phase in special designed samples designed to provoke shrinkage porosity and metal expansion penetration. It was found, that the inter-dendritic space varies within a casting. This was explained by the coarsening of the primary dendrites which originates from differences in the local time of solidification. / <p>QC 20131210</p>
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-136985 |
| Date | January 2013 |
| Creators | Svidró, Péter |
| Publisher | KTH, Tillämpad processmetallurgi, Stockholm |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Licentiate thesis, comprehensive summary, info:eu-repo/semantics/masterThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds