Cheung Lok Ying Teresa = 竹炭模板上形成的二氧化硅與碳化硅納米線及其表徵 / 張樂影. / Thesis (M.Phil.)--Chinese University of Hong Kong, 2006. / Includes bibliographical references. / Text in English; abstracts in English and Chinese. / Cheung Lok Ying Teresa = Zhu tan mo ban shang xing cheng de er yang hua gui yu tan hua gui na mi xian ji qi biao zheng / Zhang Leying. / ABSTRACT --- p.i / 摘要 --- p.iii / ACKNOWLEDGEMENTS --- p.v / TABLE OF CONTENTS --- p.vii / LIST OF FIGURE CAPTIONS --- p.xi / LIST OF TABLE CAPTIONS --- p.xv / Chapter Chapter 1 --- Introduction / Chapter 1.1. --- Biomineralization process --- p.1 / Chapter 1.2. --- Structures in biological matters --- p.2 / Chapter 1.2.1. --- Bone --- p.2 / Chapter 1.2.2. --- Wood --- p.3 / Chapter 1.3. --- Biomorphic products and their potential applications --- p.4 / Chapter 1.3.1 --- Environment conscious products --- p.4 / Chapter 1.3.2 --- Properties --- p.5 / Chapter 1.3.3 --- Carbide and oxide composites --- p.5 / Chapter 1.4 --- Common fabrication approaches --- p.6 / Chapter 1.4.1 --- Gaseous infiltration --- p.7 / Chapter 1.4.2 --- Liquid infiltration --- p.7 / Chapter 1.4.3 --- Sol-gel method --- p.8 / Chapter 1.5 --- Growth of nanowires --- p.8 / Chapter 1.5.1 --- Vapor-liquid-solid (VLS) mechanism --- p.9 / Chapter 1.5.2 --- Solution-liquid-solid (SLS) mechanism --- p.9 / Chapter 1.5.3 --- Vapor-solid (VS) mechanism --- p.10 / Chapter 1.6 --- Goals of the project --- p.10 / Chapter 1.6.1 --- Feedbacks on previous works --- p.10 / Chapter 1.6.2 --- Our breakthrough approach --- p.11 / Chapter 1.7 --- Thesis layout --- p.12 / References --- p.13 / Figures --- p.17 / Chapter Chapter 2 --- Samples preparation and characterization methods / Chapter 2.1 --- Materials selections --- p.22 / Chapter 2.1.1 --- Selection of materials for biomorphic substrate --- p.22 / Chapter 2.1.2 --- Selection of solution for infiltration --- p.23 / Chapter 2.2 --- Samples preparation --- p.24 / Chapter 2.2.1 --- Pyrolysis of raw bamboo --- p.24 / Chapter 2.2.2 --- Infiltration of reactants --- p.25 / Chapter 2.2.3 --- Sintering conditions --- p.26 / Chapter 2.3 --- Characterization methods --- p.26 / Chapter 2.3.1 --- Scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDS) --- p.27 / Chapter 2.3.2 --- Transmission electron microscopy (TEM) and EDS --- p.27 / Chapter 2.3.3 --- High-resolution transmission electron microscopy (HRTEM) --- p.27 / Chapter 2.3.4 --- X-ray diffraction (XRD) --- p.28 / Chapter 2.3.5 --- X-ray photoelectron spectroscopy (XPS) --- p.28 / Chapter 2.3.6 --- Fourier transform infrared spectroscopy (FTIR) --- p.29 / Chapter 2.4 --- Conclusions --- p.29 / References --- p.30 / Figures --- p.31 / Tables --- p.33 / Chapter Chapter 3 --- Bamboo biomorphic substrates / Chapter 3.1 --- Overview --- p.34 / Chapter 3.2 --- Volumetric shrinkage and weight loss --- p.34 / Chapter 3.3 --- General morphology --- p.35 / Chapter 3.4 --- Intrinsic impurities --- p.35 / Chapter 3.5 --- Structures --- p.36 / References --- p.38 / Figures --- p.39 / Chapter Chapter 4 --- Silica / Chapter 4.1 --- Overview --- p.43 / Chapter 4.2 --- Thermal analyses --- p.44 / Chapter 4.2.1 --- Raw biomorphic substrates --- p.44 / Chapter 4.2.2 --- Infiltrated biomorphic substrates --- p.45 / Chapter 4.3 --- Experiments --- p.46 / Chapter 4.4 --- Characterization in general --- p.47 / Chapter 4.4.1 --- General morphologies --- p.47 / Chapter 4.4.2 --- Tips of the SiO2 nanowires --- p.48 / Chapter 4.5 --- Effects of sintering duration --- p.48 / Chapter 4.6 --- Effects of sintering temperature --- p.49 / Chapter 4.6.1 --- "Different temperatures, held for one hour" --- p.50 / Chapter 4.6.2 --- "Different temperatures, held for ten hours" --- p.50 / Chapter 4.7 --- Growth mechanisms --- p.52 / Chapter 4.8 --- Summary --- p.54 / References --- p.56 / Figures --- p.58 / Tables --- p.75 / Chapter Chapter 5 --- Silicon carbide / Chapter 5.1 --- Overview --- p.76 / Chapter 5.2 --- Experiments --- p.77 / Chapter 5.3 --- Characterization in general --- p.78 / Chapter 5.3.1 --- General morphologies --- p.78 / Chapter 5.3.2 --- Stacking faults and twinning --- p.79 / Chapter 5.3.3 --- Tips of the SiC nanowires --- p.81 / Chapter 5.4 --- Growth mechanisms --- p.82 / Chapter 5.5 --- Summary --- p.83 / References --- p.84 / Figures --- p.87 / Chapter Chatper 6 --- Conclusions and future works / Chapter 6.1 --- Main results of this projects --- p.101 / Chapter 6.2 --- Future works --- p.103 / References --- p.104
| Identifer | oai:union.ndltd.org:cuhk.edu.hk/oai:cuhk-dr:cuhk_325701 |
| Date | January 2006 |
| Contributors | Cheung, Lok Ying Teresa., Chinese University of Hong Kong Graduate School. Division of Materials Science and Engineering. |
| Source Sets | The Chinese University of Hong Kong |
| Language | English, Chinese |
| Detected Language | English |
| Type | Text, bibliography |
| Format | print, xv, 104 leaves : ill. ; 30 cm. |
| Rights | Use of this resource is governed by the terms and conditions of the Creative Commons “Attribution-NonCommercial-NoDerivatives 4.0 International” License (http://creativecommons.org/licenses/by-nc-nd/4.0/) |
Page generated in 0.0027 seconds