Orientador: Francisco das Chagas Marques / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-12T20:56:17Z (GMT). No. of bitstreams: 1
Silva_DouglasSoaresda_M.pdf: 1607458 bytes, checksum: 64efea4eea6490352c0cec9182778a67 (MD5)
Previous issue date: 2009 / Resumo: Nesta tese estamos propondo o uso de carbono amorfo como um possível candidato para uso como camada antirrefletora em células solares de silício cristalino. O carbono amorfo pode ser preparado com alta banda proibida e tem propriedades importantes como alta dureza, baixo coeficiente de atrito, preparado à temperatura ambiente, etc. Além disso, o carbono amorfo é um material abundante na natureza e seu uso em eletrônica poderia reduzir o consumo de materiais tóxicos, contribuindo para reduzir danos ao meio ambiente.
Foram exploradas as propriedades óticas dos filmes de carbono e carbono de silício produzidos por diferentes métodos de deposição (RF Glow Discharge, RF Sputtering e FCVA_Filtered Cathodic Vacuum Arc) visando a aplicação como camadas antirrefletoras em células solares. O estudo de propriedades óticas dos filmes, como a banda proibida, índice de refração, coeficiente de absorção e reflexão integrada foram determinantes para as conclusões deste trabalho. Para isto foram importantes a fabricação de células solares e o estudo dos principais parâmetros fotovoltaicos: eficiência, corrente de curto circuito, tensão de circuito aberto e fator de preenchimento. As células solares de silício monocristalino foram desenvolvidas a partir da técnica amplamente difundida e conhecida através da difusão térmica de dopantes de fósforo, as chamadas homojunções pn.
Diferentes estruturas antirrefletoras à base de carbono foram estudadas e comparadas. Assim, investigamos o uso de carbono tipo diamante (diamond-like carbon DLC), carbono tipo polimérico (polimeric-like carbon ¿ PLC), carbono tetraédrico (ta-C), carbeto de silício (a-CxS ix-1:H). Para efeito de comparação com camadas antirrefletoras convencionais, adotamos o dióxido de estanho (SnO2) depositado pela técnica de spray químico.
Os resultados mostraram que filmes de carbono amorfo funcionam como camada antirefletora em células solares, embora não tenha sido possível encontrar em um único material todas as condições ideais para uma camada antirrefletora em silício cristalino. O carbeto de silício se mostrou bastante promissor como um composto à base de carbono e o próprio silício, sendo utilizado na fabricação do dispositivo e abundante na natureza. / Abstract: In this thesis we propose the use of amorphous carbon as a possible candidate for use as antireflective layer in crystalline silicon solar cells. The amorphous carbon can be prepared with high band gap and important properties such as high hardness, low coefficient of friction, prepared at room temperature, etc. Moreover, the amorphous carbon material is abundant in nature and its use in electronics could reduce the consumption of toxic materials, helping to reduce damage to the environment.
We explored the optical properties of carbon films and carbon silicon produced by different methods of deposition (RF Glow Discharge, RF Sputtering and FCVA_Filtered Cathodic Vacuum Arc) to the application as antireflective coatings in solar cells. The study of optical properties of films, such as forbidden band, index of refraction, absorption coefficient and integrated reflection were crucial to the conclusions of this work. For that, it was important the manufacture of solar cells and the study of key photovoltaic parameters: efficiency, short-circuit current, open circuit voltage and fill factor. The single crystal silicon solar cells were developed from the widely known technique of thermal diffusion of phosphorus doping, the pn homojunctions.
Different antireflective structures based on carbon were studied and compared. Thus, we investigated the use of carbon type diamond (diamond-like carbon DLC), carbon type polymer (polimeric-like carbon - PLC), tetrahedral carbon (ta-C), silicon carbide (a-CxSix-1: H). For purposes of comparison with conventional antireflective layers, we adopted the tin dioxide (SnO2) deposited by chemical spray technique.
The results showed that films of amorphous carbon layer acts as antireflective coatings in solar cells, although it was not possible to find a single material in all ideal conditions for an antireflective layer in crystalline silicon. The silicon carbide wasvery promising as a compound based on carbon and the silicon, been used in the manufacture of the device and abundant in nature. / Mestrado / Mestre em Física
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/277773 |
Date | 12 August 2018 |
Creators | Silva, Douglas Soares da, 1984- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Marques, Francisco das Chagas, 1957-, Sanchez, Manuel Cid, Cescato, Lucila Helena Deliesposte |
Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 70 f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0069 seconds