Previous issue date: 2014-07-22 / In this paper were developed polypropylene composites with coconut and sisal fibers for applications in the electric sector. The mechanical properties of composites with compositions containing from 5 to 40 % by weight of fibers, coupling agent and antioxidant were studied; and it was decided that would be used 10 % of fibers in the next formulations. Then, were studied the mechanical properties and flammability of the composites containing an UV stabilizer with flame retardant effect, aluminum trihydrate (ATH), antimony trioxide (Sb2O3), and an halogen free flame retardant additive in various amounts and was obtained a formulation with V2 classification, according to UL 94. Then three composites were formulated by increasing the amount of additives present in the formulation with V2 classification and added an impact modifier. Were then obtained a formulation with V0 classification and Izod impact resistance of (26.89 ± 1.89) J/m for composites with coconut fibers, and (25.35 ± 3.47) J/m for composite with sisal fibers. / Neste trabalho foram desenvolvidos compósitos de polipropileno com fibras de coco e sisal para aplicações no setor elétrico. Foram estudadas as propriedades mecânicas de compósitos, com composições contendo de 5 a 40% em peso de fibras, agente compatibilizante e antioxidante; e definiu-se que seriam utilizados 10 % de fibras nas próximas formulações. Foram então, estudadas as propriedades mecânicas e a inflamabilidade de compósitos contendo um anti-UV com efeito retardante de chamas, alumina tri-hidratada (ATH), trióxido de antimônio (Sb2O3) e um aditivo retardante de chamas livre de halogêneos em diversas quantidades e obteve-se uma formulação com classificação V2, conforme a UL 94. Em seguida, foram formulados mais três compósitos, aumentando-se a quantidade dos aditivos presentes na formulação com classificação V2 e adicionou-se um modificador de impacto. Obteve-se então uma formulação com classificação V0 e resistência ao impacto de (26,89 ± 1,89) J/m para os compósitos com fibras de coco e de (25,35 ± 3,47) J/m para os compósitos com fibras de sisal.
| Identifer | oai:union.ndltd.org:IBICT/oai:tede2.uepg.br:prefix/1461 |
| Date | 22 July 2014 |
| Creators | Salum, Aline Souza |
| Contributors | Pianaro, Sidnei Antonio, Radovanovic, Eduardo, Zara, Alfredo José |
| Publisher | UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Programa de Pós-Graduação em Engenharia e Ciências de Materiais, UEPG, BR, Desenvolvimento e Caracterização de Materiais |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UEPG, instname:Universidade Estadual de Ponta Grossa, instacron:UEPG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0099 seconds