Novel ceramic membrane cells of BaCe₀.₅Zr₀.₃Y₀.₁₆Zn₀.₀₄O[subscript(3-δ)] (BCZYZ), a proton-conducting oxide, have been developed for electrocatalytic ammonia synthesis. Unlike the industrial Haber-Bosch process, in this work an attempt to synthesise ammonia at atmospheric pressure has been made. The membrane cell fabricated by tape casting and solution impregnation comprises of a 200 μm-thick BCZYZ electrolyte and impregnated electrode composites. Electrocatalysts for anode and cathode were investigated. For the anode, the co-impregnation of Ni and CeO₂ provided excellent electrode performance including high catalytic activity, sintering stability and compatibility with the BCZYZ electrolyte. The best composition was the mixture of 25 wt% NiO and 10 wt% CeO₂. A symmetrical cell prepared with this electrode composition revealed low polarisation resistances of 1.0 and 0.45 Ωcm² in humidified 5% H₂/Ar at 400 and 500 °C, respectively. For the cathode, 25 wt% of impregnated Fe oxide provided a satisfactory performance in non-humidified N₂ atmosphere. Significant amounts of ammonia were produced from the single cell with Ni-CeO₂ anode and Fe oxide cathode at 400-500 °C under atmospheric pressure. Ammonia formation rate was enhanced by Pd catalyst addition and electrochemical performance was improved by Ru addition. The highest ammonia formation rate of 4 x 10⁻⁹ mols⁻¹cm⁻² was attained using the cell with a Pd-modified Fe cathode at 450 °C. The formation reaction of ammonia typically consumed around 1-2.5 % of total applied current while most of the applied current was employed in H⁺ reduction. The total current efficiency of around 90-100 % could be obtained from the membrane cells.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:552477 |
| Date | January 2010 |
| Creators | Klinsrisuk, Sujitra |
| Contributors | Irvine, John T. S. |
| Publisher | University of St Andrews |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://hdl.handle.net/10023/1294 |
Page generated in 0.0021 seconds