This thesis undertakes the development, characterization and optimization of boron diffusion for silicon solar cells. Heavy diffusions (sheet resistance < 40 Ohm/square) to form a back surface field, and light diffusions (sheet resistance > 100 Ohm/square) to form oxide-passivated emitters were developed. Test structures and solar cells were fabricated to assess uniformity, lifetime and recombination effects due to the light and heavy boron diffusions. It was found that the growth of a thin ~200 ??, thermal oxide, during stabilization ??? immediately prior to the boron diffusion - was required to maintain high lifetime and reduce surface recombination (reducing the emitter saturation current density) for all boron diffusions. The heavy boron diffusion process was incorporated into the single side buried contact solar cell processing sequence. The solar cells fabricated had both boron diffused and Al/Si alloyed P+ regions for comparison. This research conclusively showed that boron diffused solar cells had significantly higher open circuit voltage compared to Al/Si alloyed devices. Fabrication of n-type solar cells, and their subsequent characterization by overlayed secondary electron image and the electron beam induced current map showed that the Al/Si alloy varied in depth from 5 to 25 micrometers deep. Methodology and characterization for light, oxide-passivated boron diffusions are also presented. This study yielded boron diffused emitters (sheet resistance > 100 Ohm/square) with low emitter saturation current. It was observed that this was possible only when the thermal oxidation after the boron diffusion was minimal, less than 1,000 ??. This was due to the segregation effect of boron with oxide, decreasing the surface concentration that in turn decreased the electric field repulsion of electrons from the surface. Device modelling of n-type solar cells is presented where the parameters of the modelling include the results of the light, oxide-passivated boron diffusions. This modelling shows n-type-base material with light oxide-passivated boron diffusion has higher potential conversion efficiency than forming a solar cell from phosphorous diffused p-type material.
| Identifer | oai:union.ndltd.org:ADTP/258593 |
| Date | January 2005 |
| Creators | Slade, Alexander Mason, Electrical Engineering, UNSW |
| Publisher | Awarded by:University of New South Wales. Electrical Engineering |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | Copyright Alexander Mason Slade, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0019 seconds