Orientador: Roseana da Exaltação Trevisan / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-12T18:26:12Z (GMT). No. of bitstreams: 1
Fraga_FranciscoEdsonNogueira_D.pdf: 3779686 bytes, checksum: b907dc0886225032e946b10c70a7169c (MD5)
Previous issue date: 2009 / Resumo: O interesse da indústria em se ter um maior controle das distorções provocadas pela soldagem de chapas de alumínio, em função da crescente demanda por esse material, incentivaram o desenvolvimento do presente trabalho. Neste trabalho são estudadas as deformações causadas pela soldagem TIG em chapas de alumínio, liga Al 5052, em função do grau de encruamento das chapas e em função da direção de soldagem em relação ao sentido de laminação. Foram utilizadas chapas com três graus de laminação a frio e as soldas realizadas no sentido paralelo e perpendicular ao sentido de laminação das chapas. As distorções provocadas pela soldagem foram avaliadas através de uma metodologia desenvolvida nesse trabalho. Essa metodologia possibilitou a quantificação dos resultados através de coeficientes de distorção longitudinal e transversal. Complementarmente, para melhor compreensão dos resultados, procedeu-se uma análise microestrutural por microscopia ótica e por EBSD (Eletron Backscatter Diffraction) no metal base e na zona afetada pelo calor (ZAC). Com o EBSD obteve-se resultados de textura cristalográfica no metal base, que foram avaliados por meio de ODF (Orientation Distribution Function). As distorções provocadas pela soldagem foram avaliadas com um nível de significância dos resultados de 10%. Os resultados de distorção mostraram ocorrências de deformações longitudinais e transversais em todas as condições avaliadas. Foi descoberto que a direção de soldagem paralela ao sentido de laminação do material gera maior distorção, em comparação com a solda perpendicular à laminação. Essa influência da direção de soldagem foi significativamente relevante por consequência da presença da textura tipo Brass no material encruado. A influência do grau de encruamento do material sobre a quantidade de distorções foi tão relevante quando a direção de soldagem em relação à laminação. O coeficiente de distorção aumentou com o aumento do grau de encruamento das chapas. Foi caracterizado também um aumento da largura da ZAC em função do grau de laminação do material, concomitante com o aumento das distorções devido à soldagem. / Abstract: The industry interest on having a better control in the distortions provoked by welding of aluminum plates, caused by the crescent demand of this material, motivated the development of this work. In this work, it is studied the deformation caused by TIG welding in aluminum plates, alloy Al 5052, in function of the cold working degree (tempers) on the plates and in function of the welding direction in relation to the rolling direction. Were used plates with three different tempers (O, H32 and H34) and the welds were made parallel and perpendicular to the rolling direction. The welding distortions were evaluated by means of a methodology developed in this work. With this methodology was possible to quantify the results through the longitudinal and transversal distortion coefficients. Additionally, for a better understanding of the results, it was carried out a micrographic analysis by means of optical microscopy and Eletron Backscatter Diffraction (EBSD) over the base metal and the heat affected zone (HAZ). With the EBSD analysis it was obtained results about the crystallographic texture on the base metal, which were evaluated by means of Orientation Distribution Function (ODF). The distortions caused by welding were evaluated with a significance level of the results of 10%. The results of the distortions showed the occurrence of longitudinal and transversal deformations in all conditions evaluated. It was discovered that the welding direction parallel to the rolling direction of the material cause the largest distortion compared to the direction welding perpendicular to the rolling direction. This influence of the welding direction was relevant in consequence of the presence of Brass texture in the rolling material. The influence of the cold working degree of the material over the quantity of distortions was as much relevant as the welding direction in relation to the rolling direction. The distortion coefficient increased with the increase of the cold working degree of the plates. It was also verified an increase in the width of the HAF in function of the cold working degree of the material, as well as an increase of the distortions caused by the welding. / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265234 |
| Date | 12 August 2018 |
| Creators | Fraga, Francisco Edson Nogueira |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Trevisan, Roseana da Exaltação, 1951-, Zoqui, Eugênio José, Londono, Antonio Jose Ramirez, Kobayashi, Yukio, Lima, Carlos Roberto Camello |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 138 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.013 seconds