Previous issue date: 2015-12-21 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Os aços Maraging são aços de ultra-alta-resistência, tem composição à base de ferro ligado com cerca de 18% de níquel, com limite de esoamento entre 1.400 a 2.500 MPa. Possuem propriedades superiores, tais como a alta ductilidade, boa soldabilidade, tratamento térmico simples sem deformações, boa usinabilidade, alta resistência e resistência ao desgaste. A sua boa tenacidade permiti que suporte tensões repetidas de fadiga por maior tempo, comparado com outros aços de alta resistência. Para o presente trabalho, a partir de diversos testes de solda a laser, aplicação de tratamentos térmicos e tratamento superficial de nitretação a plasma, foram estudadas as propriedades mecânicas através de ensaios de tração, fadiga, impacto, dureza e rugosidade. Foram também analisadas, com auxílio do Microscópio Óptico, as características microstuturais da zona de fusão (ZF), zona térmica afetada (ZTA) pelo calor da solda e camada nitretada. Com o auxílio de um Microscópio Eletrônico de Varredura (MEV) analisou-se o mecanismo da fratura e foram realizadas análises por E.D.S. (Energia Dispersiva de Raios X). Foram realizados vários teste com tempos e temperaturas para se definir a melhor condição de envelhecimento, obteve-se a temperatura de 480°C por 3 horas como satisfatoria. A solda a laser mostrou-se eficaz para a união das chapas, com perda de resistência inferior a 10%, quando comparada com a resistência do aço maraging sem solda. As análises da superfície fraturada mostram que a ruptura dos corpos de prova soldados ocorrereu na região da zona fundida, e possui natureza dúctil, com a formação de dimples, para todas as condições de tratamento térmico, o processo de soldagem e nitretação a plasma não alteraram o tipo de fratura típica dos aços maraging. A vida em fadiga não foi prejudicada pela nitretação, porém, foi observado uma redução da vida em fadiga do material soldado comparado com o material sem solda. Os resultados indicam, que o tratamento térmico de envelhecimento elevou as propriedades mecânicas do aço maraging tanto do material soldado como do nitretetado a plasma, com valores de resistência de aproximadamente 2.000 MPa e alongamento em torno de 8%. / Maraging Steels are ultra-high-strength, that have their composition based on iron alloyed with approximately 18% Nickel, with yield strength between 1.400 to 2.400 MPa. They have superior properties, such as high ductility, good weldability, simple heat treatment without deformation, good machinability, high strength and wear resistance. Their hardness and resistance allow them to supports repeated stress of longer fatigue in comparison with other high strength steels. The maraging steel has a significant cost advantage due to the good workability, predictable and uniform retraction during heat treatment, making this steel be promising. For this work, from various laser welding tests, heat treatment and surface treatment of plasma nitriding, The mechanical properties were studied by means of testing: traction; fatigue; impact; hardness; and roughness. We also analyze, with the aid of optical microscope, the microstructural characteristics of the fusion zone (FZ), the heat affected zone (HAZ) due the welding and by nitrided layer. With the aid of SEM (Scanning Electron Microscope) and EDS (Energy Dispersive Scanning), we analyzed the fractured mechanisms. Several tests were carried out with times and temperatures to determine the best aging condition and the chosen temperature was 480°C for 3 hours. The application of laser welding seems to be effective for joining the plates with loss in the yield strength or tensile strength less than 10%, compared with the strength of maraging steel without welding. The analyses of the fractured surface showed that the rupture of the welded samples occurred in the fused zone region and has ductile nature, with formation of dimples for all heat treatment conditions. The welding and plasma nitriding process have not modified the type of typical fracture of the maraging steel. The life in fatigue was not affected by nitrided, however, they observed a reduction in fatigue life of welded material, compared with no soldering material. The results showed that aging heat treatments increased the mechanical properties of maraging steel both welded and plasma nitrided material, whit strength values about 2.000 MPa and elongation nearly 8%.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/132905 |
| Date | 21 December 2015 |
| Creators | Lombardo, Sandro [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Abdalla, Antonio Jorge [UNESP], Pereira, Marcelo dos Santos [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600 |
Page generated in 0.0028 seconds