Vliv podmínek mechanického legování na kontaminaci práškových směsí a bulk materiálů / The influence of mechanical alloying on contamination of powder mixtures and bulk materials

This thesis deals with the influence of process parameters on the contamination level of powder materials produced by mechanical alloying (MA) technology. For this purpose austenitic stainless steel 316 L and equiatomic CoCrFeNi high-entropy alloy (HEA) were prepared by high-energy ball milling. Both materials were milled in argon and nitrogen atmospheres from 5 to 30 hours. Spark plasma sintering method (SPS) was then used for consolidation of chosen powder samples. Chemical analysis of contamination within MA was carried out using combustion analysers for determination of carbon, oxygen, and nitrogen contents after different lengths of milling. Also differences in chemical composition of powder and corresponding bulk samples were measured. The microstructure analysis using scanning electron microscopy (SEM) of both powder and bulk materials was executed with focus on oxide and carbide presence and dispersion. Increasing content of carbon with increasing milling time was observed across all measured samples. This contamination is attributed to using milling vial made of tool steel AISI D2 (containing 1,55 wt. % of carbon). Increase of carbon content within consolidation using SPS was also observed. Milling of specimens using N2 as milling atmosphere caused higher contamination level in both AISI 316 L and HEA compared to milling in argon.

Identiferoai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:416663
Date January 2020
CreatorsKubíček, Antonín
ContributorsHadraba, Hynek, Moravčík, Igor
PublisherVysoké učení technické v Brně. Fakulta strojního inženýrství
Source SetsCzech ETDs
LanguageCzech
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/masterThesis
Rightsinfo:eu-repo/semantics/restrictedAccess

Page generated in 0.0014 seconds