The solid-state mesoscopic solar cells (sMSCs) have been developed as a promising alternative technology to the conventional photovoltaics. However, the device performance suffers from the low hole-mobilities and the incomplete pore filling of the hole transport materials (HTMs) into the mesoporous electrodes. A variety of HTMs and different preparation methods have been studied to overcome these limitations. There are two types of sMSCs included in this doctoral thesis, namely solid-state dye-sensitized solar cells (sDSCs) and organometallic halide perovskite based solar cells. Two different types of HTMs, namely the small molecule organic HTM spiro-OMeTAD and the conjugated polymer HTM P3HT, were compared in sDSCs. The photo-induced absorption spectroscopy (PIA) spectra and spectroelectrochemical data suggested that the dye-dye hole conduction occurs in the absence of HTM and appears to be of significant importance to the contribution of hole transport. The PIA measurements and transient absorption spectroscopy (TAS) indicated that the oxidized dye was efficiently regenerated by a small molecule organic HTM TPAA due to its excellent pore filling. The conducting polymer P3HT was employed as a co-HTM to transfer the holes away from TPAA to prohibit the charge carrier recombination and to improve the hole transport. An alternative small molecule organic HTM, MeO-TPD, was found to outperform spiro-OMeTAD in sDSCs due to its more efficient pore filling and higher hole-mobility. Moreover, an initial light soaking treatment was observed to significantly improve the device performance due to a mechanism of Li+ ion migration towards the TiO2 surface. In order to overcome the infiltration difficulty of conducting polymer HTMs, a state-of-the-art method to perform in-situ photoelectrochemical polymerization (PEP) in an aqueous micellar solution of bis-EDOT monomer was developed as an environmental-friendly alternative pathway with scale-up potential for constructing efficient sDSCs with polymer HTMs. Three different types of HTMs, namely DEH, spiro-OMeTAD and P3HT, were used to investigate the influence of HTMs on the charge recombination in CH3NH3PbI3 perovskite based sMSCs. The photovoltage decay measurements indicate that the electron lifetime (τn) of these devices decreases by one order of magnitude in the sequence τspiro-OMeTAD > τP3HT > τDEH.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-232271 |
| Date | January 2014 |
| Creators | Yang, Lei |
| Publisher | Uppsala universitet, Fysikalisk kemi, Uppsala |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Digital Comprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology, 1651-6214 ; 1181 |
Page generated in 0.0017 seconds