Influência da velocidade de deslizamento, da carga normal e da transformação martensítica induzida por deformação plástica na resistência ao desgaste por deslizamento dos aços inoxidáveis austeníticos. / Influence of sliding velocity, applied load and strain-induced martensitic transformation on the sliding wear resistance of the austenitic stainless steels.

Neste trabalho, estudaram-se os mecanismos de desgaste por deslizamento dos aços AISI 304 e AISI 316 em função da carga normal (de 6 N a 20 N) e da velocidade tangencial (de 0,07 m/s a 0,81 m/s). De acordo com o planejamento fatorial 23, realizaram-se ensaios de desgaste em equipamento convencional, do tipo pino-contra-disco. Foram usadas técnicas de análise das superfícies e das partículas após o desgaste: microscopia eletrônica de varredura (MEV), difração de raios-X, espectroscopia Mössbauer, rugosidade, temperatura e dureza instrumentada. Concluiu-se que os mecanismos de desgaste por deslizamento para os aços AISI 304 e AISI 316 são dominados pela deformação plástica (desgaste por oxidação de partículas metálicas, desgaste adesivo e desgaste misto). A variação da taxa de desgaste dos dois materiais dependeu do efeito da interação entre os níveis de carga normal e velocidade tangencial. Por meio do planejamento composto central, foi possível obter um modelo empírico da variação da taxa de desgaste em função da carga normal e da velocidade. / In this work, sliding wear mechanism of AISI 304 and AISI 316 austenitic stainless steels were studied as a function of the applied load (from 6 N to 20 N) and the tangential velocity (from 0.07 m/s to 0.81 m/s). Following the 23 factorial design, wear experiments were performed using a conventional pin-on-disc machine. Worn surfaces and wear debris analysis techniques were used: scanning electron microscopy (SEM), X-ray diffraction, Mössbauer spectroscopy, stylus profiling, surface temperature measurement and instrumented indentation. Plasticity-dominated wear (metallic debris oxidation, adhesive wear and mixed wear) are the sliding wear mechanisms for AISI 304 and AISI 316 steels. The wear rate behavior depended on interaction effect between applied load and tangential velocity. An empirical model of wear rate as a function of applied load and tangential velocity was obtained by means of the central composite design.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-19072005-131103
Date02 December 2004
CreatorsMoré Farías, María Cristina
ContributorsTanaka, Deniol Katsuki
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguagePortuguese
TypeTese de Doutorado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0022 seconds