Torneamento do aço inoxidável super duplex UNS S32750 e influência na resistência à corrosão / UNS S32750 super duplex stainless stell turning and its influence in the corrosion resistance

Orientador: Anselmo Eduardo Diniz / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-22T09:27:39Z (GMT). No. of bitstreams: 1
OliveiraJunior_CarlosAncelmo_M.pdf: 7354499 bytes, checksum: 05a6c099baa7c4f194f916c8e418d4db (MD5)
Previous issue date: 2013 / Resumo: Os aços inoxidáveis super duplex são ligas extremamente resistentes à corrosão, desenvolvidas para aplicações com altos níveis de exigência, em que as peças terão contato com ambientes corrosivos como a água do mar, por exemplo. Devido à sua composição química e microestrutura, que proporcionam alta resistência mecânica, alta resistência ao calor e também alta ductilidade, que são fatores positivos para a aplicação, a usinabilidade dessas ligas é geralmente muito baixa o que resulta em longos ciclos de produção e alto custo de ferramental. Este trabalho trata do torneamento da liga UNS 32750 comercialmente conhecida como SAF2507 e sua consequente influência na resistência à corrosão apresentada ao longo da aplicação. Durante os ensaios, houve variação de velocidade de corte, classe e cobertura da ferramenta, além da condição de refrigeração com alternativas de alta e baixa pressão. Os resultados indicam que as pastilhas com cobertura PVD são mais resistentes ao desgaste e, combinadas ao uso de refrigeração de alta pressão, podem melhorar o seu desempenho em relação à vida útil e rugosidade bem como à posterior resistência à corrosão do material. Desgaste de entalhe e aderência encontrados na usinagem com pastilhas PVD, juntamente com lascamentos e quebras que ocorreram nas pastilhas CVD, foram os tipos e mecanismos de desgaste/avaria da ferramenta mais encontrados durante os ensaios / Abstract: Super duplex stainless steels are extremely corrosion-resistant alloys that were developed to work in very demanding applications, in which the workpieces are exposed to corrosive environments like sea water, for example. Due to their chemical composition and microstructure, that provide high mechanical and heat resistance besides high ductility, which are favorable factors for the application, the machinability of these alloys is generally poor and results in long production cycles and high tool costs. The goal of this research is to study turning operation of the UNS 32750 alloy, commercially called SAF2507, and its consequent influence in the corrosion resistance for application situations. During the tests, the input variables were cutting speed, grade and coating of the inserts, besides the cooling conditions with low and high pressure options. The results indicate that the PVD coated inserts are more wear-resistant than the CVD inserts and when they are combined with high pressure cooling, their performance related to tool life and workpiece roughness as well as the corrosion resistance of the material after machining is improved. Notch wear and attrition found in machining with PVD inserts, together with chipping and tool breakage that occurred in machining with CVD inserts, were the most frequent types of wear/damage and wear mechanism found during the tests / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/264188
Date22 August 2018
CreatorsOliveira Junior, Carlos Ancelmo, 1981-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Diniz, Anselmo Eduardo, 1959-, Ferreira, João Roberto, Robert, Maria Helena
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format107 p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds