In this study, by considering different mechanical properties such as wear resistance and toughness of two different metal alloys in design and production stages, bi-metal casting technique was used for producing composite material which will be a solution for the cracking and wear problem in coal crushing hammer heads. The failure analysis of the classical hammer heads which are made from Hadfield steels (austenitic steel) showed that there are crack formations through austenitic grains and also the phase transformation from austenite to martensite is not completed until the material consumed its life.
Thermal analysis is the basic technique in this study to determine the solidification conditions. By using thermocouples with a suitable set-up, the cooling curves of the materials which were used in bi-metal casting had been taken and analysed. By using these cooling curve data with a written software program which is based on Newton Thermal Analysis, the solid fraction values by time and by temperate were obtained. According to these values, the interface was investigated by changing experimental conditions and solid fractions. At the last part of the study, a new approach was tried in white cast iron production.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/2/12609925/index.pdf |
| Date | 01 September 2008 |
| Creators | Kirma, Turgut |
| Contributors | Selcuk, Ekrem |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for METU campus |
Page generated in 0.0017 seconds